PPO PX9406-111 SABIC INNOVATIVE SHANGHAI
NORYL™
Automotive interior parts
Flame retardant、Characteristics: Flame re、HDT/1.8、122°C
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Basic performance | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/PX9406-111 |
|---|---|---|---|
| Water absorption rate | 24hrs | ASTM D-570 | 0.06 % |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/PX9406-111 |
|---|---|---|---|
| Flexural modulus | 6.4mm | ASTM D-790 | 2646 Mpa |
| Impact strength of cantilever beam gap | 23°C | ASTM D-256 | 160 J/m |
| tensile strength | 断裂点，3.2mm | ASTM D-638 | 18 Mpa |
| bending strength | 6.4mm | ASTM D-790 | 112 Mpa |
| tensile strength | 屈服点，3.2mm | ASTM D-638 | 75 Mpa |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/PX9406-111 |
|---|---|---|---|
| Volume resistivity | ASTM D-257 | 2.0×10 Ω.cm | |
| dielectric constant | 1MHz | ASTM D-150 | 2.49 |
| Surface Resistivity | ASTM D-257 | 1.0×10 Ω.cm |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/PX9406-111 |
|---|---|---|---|
| density | ASTM D-792 | 1.11 | |
| UL flame retardant rating | UL 94 | 0.8 mm | |
| UL 94 | V-0 | ||
| Shrinkage rate | 3.2mm | ASTM D-955 | 5-7 10 |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/PX9406-111 |
|---|---|---|---|
| Long term use temperature | 无冲击 | UL 746B | 105 °C |
| Heat distortion temperature | 1.8MPa，HDT | ASTM D-648 | 122 °C |
| 0.45MPa，HDT | ASTM D-648 | 133 °C | |
| vicat | ASTM D-1525 | 150 °C | |
| Long term use temperature | 含冲击 | UL 746B | 100 °C |
| 电气 | UL 746B | 105 °C |