PA/MXD6 1002H MITSUBISHI ENGINEERING JAPAN
RENY™ 
Electronic and Electrical、Automotive sector
High rigidity、High impact、Filler: Glass fiber reinf、30%、Filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/1002H
Impact strength of simply supported beam without notch23°CISO 17935 kJ/m²
Electrical performanceTest ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/1002H
dielectric strength1.00mmIEC 60243-131 KV/mm
Volume resistivityIEC 600931E+16 ohms·cm
relative permittivity100HzIEC 60250--
Dissipation Factor100HzIEC 60250--
dielectric strength2.00mmIEC 60243-127 KV/mm
relative permittivity1MHzIEC 60250--
Surface ResistivityIEC 600937E+14 ohms
Dissipation Factor1MHzIEC 60250--
Compared to the Leakage Tracking Index (CTI)IEC 60112 V
Mechanical propertiesTest ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/1002H
Tensile modulusISO 527-212100 Mpa
bending strengthISO 178286 Mpa
Tensile strain断裂ISO 527-21.7 %
Flexural modulusISO 17811600 Mpa
tensile strength 断裂ISO 527-2181 Mpa
flammabilityTest ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/1002H
UL flame retardant rating1.6mmUL 94HB
physical property Test ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/1002H
Shrinkage rate0.51 %
Melt volume flow rate275°C/2.16kgISO 113331.0 cm3/10min
Water absorption rate平衡,23°C,50%RHISO 621.5 %
饱和,23°CISO 620.20 %
melt mass-flow rate275°C/2.16kgISO 113341 g/10min
Thermal performanceTest ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/1002H
Heat distortion temperature0.45MPa,未退火，HDTISO 75-2/B237 °C
1.8MPa,未退火，HDTISO 75-2/A224 °C
Linear coefficient of thermal expansionMDISO 11359-22E-05 cm/cm/°C
TDISO 11359-25E-05 cm/cm/°C