Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC HFD4412 BK1E707 SABIC INNOVATIVE NANSHA
LEXAN™
Architectural Application、Plastic bag
High mobility
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/HFD4412 BK1E707 |
|---|---|---|---|
| Vicat Softening Temperature | ISO 306/B120 | 143 °C | |
| RTI | UL 746 | 80.0 °C | |
| Deflection Temperature Under Load? | 1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 7 | ISO 75-2/Af | 127 °C |
| Linear thermal expansion coefficient | 横向 : -40 到 40°C | ASTM E831 | 7.0E-5 cm/cm/°C |
| Ball PressureTest | 123 到 127°C | IEC 60695-10-2 | 通过 |
| Linear thermal expansion coefficient | 流动 : 23 到 80°C | ISO 11359-2 | 3.0E-5 cm/cm/°C |
| RTI Imp | UL 746 | 80.0 °C | |
| RTI Elec | UL 746 | 80.0 °C | |
| Deflection Temperature Under Load? | 1.8 MPa, 未退火, 3.20 mm | ASTM D648 | 125 °C |
| Linear thermal expansion coefficient | 流动 : -40 到 40°C | ASTM E831 | 3.0E-5 cm/cm/°C |
| Deflection Temperature Under Load? | 0.45 MPa, 未退火, 3.20 mm | ASTM D648 | 130 °C |
| Linear thermal expansion coefficient | 横向 : 23 到 80°C | ISO 11359-2 | 7.0E-5 cm/cm/°C |
| Injection | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/HFD4412 BK1E707 |
|---|---|---|---|
| Middle Temperature | 275 到 300 °C | ||
| Drying Time | 3.0 到 4.0 hr | ||
| Suggested Shot Size | 40 到 60 % | ||
| Drying Temperature | 120 °C | ||
| Mold Temperature | 70 到 95 °C | ||
| Vent Depth | 0.025 到 0.076 mm | ||
| Suggested Max Moisture | 0.020 % | ||
| Processing (Melt) Temp | 290 到 310 °C | ||
| Rear Temperature | 265 到 290 °C | ||
| Nozzle Temperature | 280 到 305 °C | ||
| Front Temperature | 290 到 310 °C | ||
| Back Pressure | 0.300 到 0.700 Mpa | ||
| Screw Speed | 40 到 70 rpm |
| Physical | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/HFD4412 BK1E707 |
|---|---|---|---|
| Moisture Absorption | 平衡, 23°C, 50% RH | ISO 62 | 0.12 % |
| Melt Mass-Flow Rate | 300°C/1.2 kg | ASTM D1238 | 15 g/10 min |
| Modeling Shrinkage | 横向流动 : 3.20 mm | 内部方法 | 0.10 到 0.30 % |
| 流动 : 3.20 mm | 内部方法 | 0.10 到 0.30 % | |
| Moisture Absorption | 饱和, 23°C | ISO 62 | 0.30 % |
| Melt Volume flow Rate | 300°C/1.2 kg | ISO 1133 | 14.0 cm3/10min |
| Mechanical Properties | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/HFD4412 BK1E707 |
|---|---|---|---|
| Tensile Elongation | 屈服 | ISO 527-2/5 | 2.8 % |
| 断裂 | ISO 527-2/5 | 2.7 % | |
| Flexural Strength | 屈服, 50.0 mm 跨距 | ASTM D790 | 159 Mpa |
| Tensile Modulus | ASTM D638 | 6400 Mpa | |
| Tensile Strength | 断裂 | ISO 527-2/5 | 110 Mpa |
| Tensile Elongation | 屈服 3 | ASTM D638 | 3.0 % |
| Tensile Strength | 屈服 3 | ASTM D638 | 96.0 Mpa |
| 屈服 | ISO 527-2/5 | 110 Mpa | |
| Flexural Modulus | 50.0 mm 跨距 | ASTM D790 | 5850 Mpa |
| Tensile Strength | 断裂 3 | ASTM D638 | 96.0 Mpa |
| Impact Properties | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/HFD4412 BK1E707 |
|---|---|---|---|
| Unnotched Izod Impact Strength | 23°C | ASTM D4812 | 830 J/m |
| -30°C 6 | ISO 180/1U | 40 kJ/m² | |
| Instrumented Dart Impact | 23°C, Total Energy | ASTM D3763 | 21.0 J |
| Charpy Unnotched Impact Strength | -30°C | ISO 179/1eU | 48 kJ/m² |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 8.0 kJ/m² |
| 23°C | ISO 179/1eA | 8.0 kJ/m² | |
| Charpy Unnotched Impact Strength | 23°C | ISO 179/1eU | 43 kJ/m² |
| Unnotched Izod Impact Strength | 23°C 6 | ISO 180/1U | 42 kJ/m² |
| Flammability | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/HFD4412 BK1E707 |
|---|---|---|---|
| Glow Wire Ignition Temperature | 1.0 mm | IEC 60695-2-13 | 850 °C |
| UL flame retardant rating | 0.30 mm | UL 94 | HB |
| Glow Wire Flammability Index | 2.0 mm | IEC 60695-2-12 | 960 °C |