PC EXL1414H SABIC INNOVATIVE US
LEXAN™
currency、Electrical field、Electronic field
Processability、Moderate liquidity、Ductility、copolymer、Good demolding performanc
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE US/EXL1414H |
|---|---|---|---|
| Heat Deflection Temperature | 1.8MPa,Unannealed,100mmSpan | ISO75-2/Ae | 128 °C |
| Vicat Softening Temperature | -- | ISO306/B50 | 145 °C |
| Ball PressureTest | 125°C | IEC60695-10-2 | Pass |
| Heat Deflection Temperature | 0.45MPa,未退火,3.20mm | ASTMD648 | 139 °C |
| Linear thermal expansion coefficient | TD：-40到40°C | ASTME831 | 7E-05 cm/cm/°C |
| Heat Deflection Temperature | 0.45MPa,Unannealed,100mmSpan | ISO75-2/Be | 140 °C |
| 1.8MPa,未退火,3.20mm | ASTMD648 | 124 °C | |
| Vicat Softening Temperature | ASTMD152510 | 145 °C | |
| -- | ISO306/B120 | 146 °C | |
| Linear thermal expansion coefficient | MD：23到80°C | ISO11359-2 | 7.2E-05 cm/cm/°C |
| TD：23to80°C | ISO11359-2 | 7.2E-05 cm/cm/°C | |
| MD：-40到40°C | ASTME831 | 7E-05 cm/cm/°C |
| Physical | Test Condition | Test Method | SABIC INNOVATIVE US/EXL1414H |
|---|---|---|---|
| Moisture Absorption | 平衡,23°C,50%RH | ISO62 | 0.15 % |
| Modeling Shrinkage | MD：3.20mm | 内部方法 | 0.40to0.80 % |
| Melt Mass-Flow Rate | 300°C/1.2kg | ASTMD1238 | 10 g/10min |
| Melt Volume flow Rate | 300°C/1.2kg | ISO1133 | 9.00 cm3/10min |
| Moisture Absorption | 饱和,23°C | ISO62 | 0.35 % |
| Mechanical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/EXL1414H |
|---|---|---|---|
| Flexural Modulus | 50.0mm跨距 | ASTMD790 | 2230 Mpa |
| Tensile Stress | 断裂 | ISO527-2/50 | 60.0 Mpa |
| Tensile Elongation | 断裂 | ASTMD638 | 98 % |
| Tensile Strain | 断裂 | ISO527-2/50 | 120 % |
| Tensile Modulus | ISO527-2/1 | 2150 Mpa | |
| Tensile Strength | 屈服 | ASTMD638 | 56.0 Mpa |
| Flexural Modulus | ISO178 | 2250 Mpa | |
| Flexural Strength | 屈服,50.0mm跨距 | ASTMD790 | 92.0 Mpa |
| Tensile Elongation | 屈服 | ASTMD638 | 6.0 % |
| Tensile Stress | 屈服 | ISO527-2/50 | 57.0 Mpa |
| Tensile Strain | 屈服 | ISO527-2/50 | 6.0 % |
| Flexural Strength | ISO178 | 85.0 Mpa | |
| Tensile Modulus | ASTMD638 | 2020 Mpa | |
| Tensile Strength | 断裂 | ASTMD638 | 50.0 Mpa |
| Impact Properties | Test Condition | Test Method | SABIC INNOVATIVE US/EXL1414H |
|---|---|---|---|
| Notched Izod Impact Strength | -30°C | ISO180/1A | 60 kJ/m² |
| Instrumented Dart Impact | -30°C,TotalEnergy | ASTMD3763 | 77.0 J |
| Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | NoBreak |
| Unnotched Izod Impact Strength | -30°C | ISO180/1U | NoBreak |
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 65 kJ/m² |
| Instrumented Dart Impact | 23°C,TotalEnergy | ASTMD3763 | 70.0 J |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 70 kJ/m² |
| Charpy Unnotched Impact Strength | 23°C | ISO179/1eU | NoBreak |
| Unnotched Izod Impact Strength | 23°C | ISO180/1U | NoBreak |
| Notched Izod Impact Strength | 23°C | ISO180/1A | 70 kJ/m² |