PLA A 4100 CL FKuR Kunststoff GmbH
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | FKuR Kunststoff GmbH/A 4100 CL |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 3.0 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 44 kJ/m² |
| film | Test Condition | Test Method | FKuR Kunststoff GmbH/A 4100 CL |
|---|---|---|---|
| OTr | 20µm | ISO 15105-2 | 130 cm³/m²/24hr |
| Water Vapor Transmission Rate | ISO 15106-3 | 170 g/m²/24hr | |
| Nitrogen transfer rate | 25µm | DIN 53380-2 | 65.0 cm³/m²/24hr |
| Mechanical properties | Test Condition | Test Method | FKuR Kunststoff GmbH/A 4100 CL |
|---|---|---|---|
| tensile strength | -- | ISO 527 | 44.0 MPa |
| Tensile modulus | ISO 527-2 | 1840 MPa | |
| tensile strength | 断裂 | ISO 527-2 | 22.0 MPa |
| Tensile strain | 断裂 | ISO 527-2 | 12 % |
| bending strength | 3.5%应变 | ISO 178 | 48.0 MPa |
| Tensile strain change rate | ISO 527 | 5.0 % | |
| Fracture bending strain | ISO 178 | Nobreak % | |
| Flexural modulus | ISO 178 | 1770 MPa |
| physical property | Test Condition | Test Method | FKuR Kunststoff GmbH/A 4100 CL |
|---|---|---|---|
| Melt volume flow rate | 190°C/2.16kg | ISO 1133 | 5.50to9.00 cm³/10min |
| Apparent density | ISO 60 | 0.82 g/cm³ | |
| density | ISO 1183 | 1.24 g/cm³ | |
| melt mass-flow rate | 190°C/2.16kg | ISO 1133 | 6.0to10 g/10min |
| Thermal performance | Test Condition | Test Method | FKuR Kunststoff GmbH/A 4100 CL |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 40.0 °C |
| vicat | ISO 306/A | 44.0 °C | |
| melting temperature | ISO 3146 | >155 °C |