Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
LDPE AT 505 CELANESE USA
--
sealant,adhesive,film
High mobility,Bondable
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| film | Test Condition | Test Method | CELANESE USA/AT 505 |
|---|---|---|---|
| tensile strength | MD:断裂,150µm | ASTM D882 | 21.0 Mpa |
| Secant modulus | 1%正割,TD:150µm | ASTM D882 | 220 Mpa |
| elongation | MD:断裂,150µm | ASTM D882 | 580 % |
| Secant modulus | 1%正割,MD:150µm | ASTM D882 | 200 Mpa |
| Dart impact | 150µm | ASTM D1709 | 300 g |
| tensile strength | MD:屈服,150µm | ASTM D882 | 11.0 Mpa |
| TD:断裂,150µm | ASTM D882 | 21.0 Mpa | |
| elongation | TD:断裂,150µm | ASTM D882 | 670 % |
| tensile strength | TD:屈服,150µm | ASTM D882 | 11.0 Mpa |
| Mechanical properties | Test Condition | Test Method | CELANESE USA/AT 505 |
|---|---|---|---|
| tensile strength | MD，150 µm，断裂 | ASTM D-882 | 21 MPa |
| elongation at break | TD | 670 | |
| MD，150 µm | ASTM D-882 | 580 % | |
| tensile strength | TD，断裂 | 21 | |
| Secant modulus | TD，1%应变 | 220 | |
| Dart impact | 150 µm | ASTM D-1709 | 300 g |
| tensile strength | 屈服,TD | 11 |
| optical performance | Test Condition | Test Method | CELANESE USA/AT 505 |
|---|---|---|---|
| gloss | 45°,150µm | ASTM D2457 | 35 |
| Haze ratio | 150µm | ASTM D1003 | 20 % |
| physical property | Test Condition | Test Method | CELANESE USA/AT 505 |
|---|---|---|---|
| melt mass-flow rate | 190℃/2.16kg | ASTM D-1238 | 0.30 g/10min |
| 190°C/2.16kg | ASTM D1238 | 0.30 g/10min |
| Thermal performance | Test Condition | Test Method | CELANESE USA/AT 505 |
|---|---|---|---|
| melting temperature | ℃ | 112 °C | |
| DSC | 112 °C |