TPE EL630 DSM HOLAND
Arnite® 
Automotive sector,Electrical appliances,Electronic field,Electrical field
transparent
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

hardnessTest ConditionTest MethodDSM HOLAND/EL630
Shore hardnessShore D, 3 SecISO 86855
thermal performanceTest ConditionTest MethodDSM HOLAND/EL630
Hot deformation temperature0.45 MPa, UnannealedISO 75-2/B115 °C
Linear coefficient of thermal expansionAcross FlowISO 11359-21.9E-4 cm/cm/°C
FlowISO 11359-21.9E-4 cm/cm/°C
Melting temperatureISO 11357-3210 °C
Vicat softening temperatureISO 306/B50125 °C
mechanical propertiesTest ConditionTest MethodDSM HOLAND/EL630
Nominal tensile fracture strainISO 527-2500 %
Tensile modulusISO 527-2280 Mpa
tensile strength100% StrainISO 527-218.0 Mpa
5.0% StrainISO 527-211.9 Mpa
50% StrainISO 527-218.6 Mpa
BreakISO 527-236.0 Mpa
10% StrainISO 527-216.9 Mpa
Electrical performanceTest ConditionTest MethodDSM HOLAND/EL630
Compared to the anti leakage trace indexIEC 60112PLC 0
Dielectric strengthIEC 60243-122 KV/mm
Dissipation factor100 HzIEC 602500.011
1 MHzIEC 602500.034
Relative permittivity100 HzIEC 602503.80
1 MHzIEC 602503.40
Volume resistivityIEC 600931.0E+14 ohms·cm
Physical propertiesTest ConditionTest MethodDSM HOLAND/EL630
Apparent densityISO 600.77 g/cm³
Melt Volume Flow Rate (MVR)230°C/2.16 kgISO 113323.0 cm3/10min
Shrinkage rate横向FlowISO 294-42.0 %
FlowISO 294-41.8 %
Water absorption rateSaturation, 23°CISO 620.60 %
Equilibrium, 23°C, 50% RHISO 620.20 %
flammabilityTest ConditionTest MethodDSM HOLAND/EL630
Flammability levelUL 94HB