Material Comparison

Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC E-2000VUR MITSUBISHI THAILAND
IUPILON™ 
Electrical applications、Home appliance components、Fitness equipment
Weather resistance
TDS
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodMITSUBISHI THAILAND/E-2000VUR
Impact strength of simply supported beam without notch23°CISO 179NoBreak
Mechanical propertiesTest ConditionTest MethodMITSUBISHI THAILAND/E-2000VUR
Tensile modulusISO 527-22400 Mpa
Nominal tensile fracture strainISO 527-2110 %
bending strengthISO 17893.0 Mpa
Flexural modulusISO 1782300 Mpa
Tensile strain屈服ISO 527-25.4 %
tensile strength 屈服ISO 527-260.0 Mpa
Electrical performanceTest ConditionTest MethodMITSUBISHI THAILAND/E-2000VUR
dielectric strength1.00mmIEC 60243-131 KV/mm
Volume resistivityIEC 600933E+16 ohms·cm
relative permittivity100HzIEC 602503.10
Dissipation Factor100HzIEC 602506E-04
dielectric strength3.00mmIEC 60243-118 KV/mm
relative permittivity1MHzIEC 602503.10
Surface ResistivityIEC 600936E+15 ohms
Compared to the Leakage Tracking Index (CTI)CTIUL 746PLC 2
Dissipation Factor1MHzIEC 602509E-03
otherTest ConditionTest MethodMITSUBISHI THAILAND/E-2000VUR
characteristic高粘度.高刚性
purpose电工电子器材
physical property Test ConditionTest MethodMITSUBISHI THAILAND/E-2000VUR
Shrinkage rateTD:3.20mm0.50-0.70 %
Melt volume flow rate300°C/1.2kgISO 11335.00 cm3/10min
Shrinkage rateMD:3.20mm0.50-0.70 %
Water absorption rate饱和,23°CISO 620.24 %
melt mass-flow rate300°C/1.2kgISO 11335.3 g/10min
Thermal performanceTest ConditionTest MethodMITSUBISHI THAILAND/E-2000VUR
Heat distortion temperature0.45MPa,未退火，HDTISO 75-2/B145 °C
1.8MPa,未退火，HDTISO 75-2/A131 °C
Linear coefficient of thermal expansionMDISO 11359-26.5E-05 cm/cm/°C
TDISO 11359-26.6E-05 cm/cm/°C