Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
POM 500P NC010 DuPont, European Union
Delrin®
Automotive sector、Fitness equipment
High rigidity、Aging resistance、currency、Weather resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | DuPont, European Union/500P NC010 |
|---|---|---|---|
| Multi axis Instrumented Impact Energy | 23°C | ISO6603-2 | 3.00 J |
| -30°C | ISO180/1U | 250 kJ/m² | |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 9.0 kJ/m² |
| Impact strength of cantilever beam gap | -30°C | ISO180/1A | 8.0 kJ/m² |
| 23°C | ISO180/1A | 9.0 kJ/m² | |
| Multi axis Instrumented Peak Impact Force | 23°C | ISO6603-2 | 2000 N |
| 23°C | ISO180/1U | 280 kJ/m² | |
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 8.0 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO179/1eU | 320 kJ/m² |
| -30°C | ISO179/1eU | 280 kJ/m² |
| Supplementary Information | Test Condition | Test Method | DuPont, European Union/500P NC010 |
|---|---|---|---|
| Emission | VDA275 | <8.00 mg/kg | |
| Emissions of Organic Compounds | VDA277 | 3.10 µgC/g |
| hardness | Test Condition | Test Method | DuPont, European Union/500P NC010 |
|---|---|---|---|
| Rockwell hardness | M计秤 | ISO2039-2 | 92 |
| H358/30 | ISO2039-1 | 192 Mpa | |
| Rockwell hardness | R计秤 | ISO2039-2 | 120 |
| Mechanical properties | Test Condition | Test Method | DuPont, European Union/500P NC010 |
|---|---|---|---|
| Nominal tensile fracture strain | ISO527-2 | 30 % | |
| Bending stress | 3.5%应变 | ISO178 | 80.0 Mpa |
| TensileCreepModule | 1hr | ISO899-1 | 2800 Mpa |
| Tensile stress | 屈服 | ISO527-2 | 71.0 Mpa |
| Tensile strain | 屈服 | ISO527-2 | 17 % |
| Tensile modulus | ISO527-2 | 3100 Mpa | |
| Flexural modulus | ISO178 | 3000 Mpa | |
| Poisson's ratio | ISO527 | 0.35 | |
| Tensile creep modulus | 1000hr | ISO899-1 | 1600 Mpa |
| Electrical performance | Test Condition | Test Method | DuPont, European Union/500P NC010 |
|---|---|---|---|
| Surface Resistivity | IEC60093 | 4E+14 ohms | |
| Dissipation Factor | 1MHz | IEC60250 | 5.5E-03 |
| CTI | IEC60112 | 600 V | |
| 1MHz | IEC60250 | 3.80 | |
| Volume resistivity | IEC60093 | 2E+14 ohms·cm | |
| dielectric strength | IEC60243-1 | 44 KV/mm | |
| 100Hz | IEC60250 | 3.80 | |
| Dissipation Factor | 100Hz | IEC60250 | 9E-03 |
| flammability | Test Condition | Test Method | DuPont, European Union/500P NC010 |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL94 | HB |
| atomization | F-value(refraction) | ISO6452 | 90 % |
| FMVSS flammability | FMVSS302 | B | |
| Burning rate 3 | 1.00mm | ISO3795 | 20 mm/min |
| UL flame retardant rating | 1.5mm | IEC60695-11-10,-20 | HB |
| Limiting Oxygen Index | ISO4589-2 | 22 % | |
| atomization | G-value(condensate) | ISO6452 | 3.5E-04 g |
| UL flame retardant rating | 0.8mm | UL94 | HB |
| 0.8mm | IEC60695-11-10,-20 | HB |
| physical property | Test Condition | Test Method | DuPont, European Union/500P NC010 |
|---|---|---|---|
| Shrinkage rate | TD | ISO294-4 | 1.9 % |
| Water absorption rate | 饱和,23°C,2.00mm | ISO62 | 1.4 % |
| MediumDensity | 1.19 g/cm³ | ||
| melt mass-flow rate | ISO1133 | 15 g/10min | |
| Melt volume flow rate | 190°C/2.16kg | ISO1133 | 13.0 cm3/10min |
| Shrinkage rate | MD | ISO294-4 | 2.0 % |
| density | ISO1183 | 1.42 g/cm³ | |
| Water absorption rate | 平衡,23°C,2.00mm,50%RH | ISO62 | 0.40 % |
| ThermalConductivityofMelt | 0.24 W/m/K |
| Thermal performance | Test Condition | Test Method | DuPont, European Union/500P NC010 |
|---|---|---|---|
| MD：-40to23°C | ISO11359-2 | 9E-05 cm/cm/°C | |
| 0.45MPa,未退火 | ISO75-2/B | 160 °C | |
| vicat | ISO306/B50 | 155 °C | |
| TD：-- | ISO11359-2 | 1E-04 cm/cm/°C | |
| 1.8MPa,未退火 | ISO75-2/A | 95.0 °C | |
| melting temperature | ISO11357-3 | 178 °C | |
| Linear coefficient of thermal expansion | TD：AnnealingTime-Optional | ISO11359-2 | 30.0 min/mm |
| MD：-- | ISO11359-2 | 1E-04 cm/cm/°C | |
| TD：-40to23°C | ISO11359-2 | 9E-05 cm/cm/°C | |
| TD：EffectiveThermalDiffusivity | ISO11359-2 | 9E-08 m²/s | |
| Linear coefficient of thermal expansion | TD：AnnealingTemperature | ISO11359-2 | 160 °C |
| BallPressure Test | 165°C | IEC60695-10-2 | Pass |