PPS XP-2130A Samsung Cheil South Korea
INFINO®
Automotive Applications、Laptop case
enhance、Flame retardant、Filler: Glass fiber reinf
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PPS/Samsung Cheil South Korea/XP-2130A
Ash Content
--
ISO3451
%
3
Ash Content
--
ASTMD5630
%
3
density
ASTMD792
g/cm³
1
density
ISO1183
g/cm³
1
Melt mass flow rate
315°C/5.0kg
ASTMD1238
g/10min
1
Melt mass flow rate
315°C/5.0kg
ISO1133
g/10min
1
Shrinkage rate
MD：3.20mm
ASTMD955
%
0
Shrinkage rate
TD：3.20mm
ASTMD955
%
0
Shrinkage rate
TD:3.20mm
ISO2577
%
0
Shrinkage rate
MD:3.20mm
ISO2577
%
0
Mechanical performance
Test Condition
Test Method
Unit
PPS/Samsung Cheil South Korea/XP-2130A
Impact strength of simply supported beam gap
23°C
ISO179/1eA
kJ/m²
1
Tensile modulus
ASTMD638
Mpa
5
Tensile modulus
ISO527-2/5
Mpa
8
tensile strength
屈服
ASTMD638
Mpa
1
tensile strength
屈服
ISO527-2/5
Mpa
1
tensile strength
断裂
ASTMD638
Mpa
1
tensile strength
断裂
ISO527-2/5
Mpa
1
elongation
断裂
ASTMD638
%
3
elongation
断裂
ISO527-2/5
%
3
Bending modulus
ASTMD790
Mpa
9
Bending modulus
ISO178
Mpa
1
Bending strength
ASTMD790
Mpa
2
Bending stress
ISO178
Mpa
1
Impact strength of cantilever beam gap
23°C,3.18mm
ASTMD256
J/m
8
Impact strength of cantilever beam gap
23°C,6.35mm
ASTMD256
J/m
7
Suspended wall beam gap impact strength
23°C
ISO180/1A
kJ/m²
1
Thermal performance
Test Condition
Test Method
Unit
PPS/Samsung Cheil South Korea/XP-2130A
Hot deformation temperature
0.45MPa,未退火,6.40mm
ASTMD648
°C
2
Hot deformation temperature
0.45MPa,Unannealed,4.00mm
ISO75-2/B
°C
2
Hot deformation temperature
1.8MPa,未退火,6.40mm
ASTMD648
°C
2
Hot deformation temperature
1.8MPa,Unannealed,4.00mm
ISO75-2/A
°C
2