Certificates
PS Luranyl® KR 2454/3 G2 ROMIRA GERMANY
--
--
Filler, glass fiber reinforced material, 10%, filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | ROMIRA GERMANY/Luranyl® KR 2454/3 G2 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 10 kJ/m² |
| -30°C | ISO 179/1eA | 10 kJ/m² | |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 35 kJ/m² |
| -30°C | ISO 179/1eU | 35 kJ/m² |
| Mechanical properties | Test Condition | Test Method | ROMIRA GERMANY/Luranyl® KR 2454/3 G2 |
|---|---|---|---|
| tensile strength | 屈服,23°C | ISO 527-2/5 | 75.0 MPa |
| Tensile strain | 断裂,23°C | ISO 527-2/5 | 4.0 % |
| Tensile modulus | 23°C | ISO 527-2/1 | 4500 MPa |
| bending strength | 23°C | ISO 178 | 140 MPa |
| flammability | Test Condition | Test Method | ROMIRA GERMANY/Luranyl® KR 2454/3 G2 |
|---|---|---|---|
| UL flame retardant rating | 1.60mm | UL 94 | V-1 |
| physical property | Test Condition | Test Method | ROMIRA GERMANY/Luranyl® KR 2454/3 G2 |
|---|---|---|---|
| Shrinkage rate | 23°C,3.20mm | ISO 294-4 | 0.30to0.50 % |
| Water absorption rate | 23°C,24hr | ISO 62 | <0.10 % |
| density | ISO 1183 | 1.20 g/cm³ | |
| Melt volume flow rate | 250°C/21.6kg | ISO 1133 | 15.0 cm³/10min |
| Thermal performance | Test Condition | Test Method | ROMIRA GERMANY/Luranyl® KR 2454/3 G2 |
|---|---|---|---|
| thermal conductivity | DIN 52612 | 0.21 W/m/K | |
| vicat | ISO 306/B50 | 138 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 133 °C |
| Linear coefficient of thermal expansion | MD：23到80°C | ISO 11359-2 | 4.0E-6到5.0E-6 cm/cm/°C |