PC/ABS XCY630 76701 SABIC INNOVATIVE US
CYCOLAC™
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE US/XCY630 76701 |
|---|---|---|---|
| Linear thermal expansion coefficient | TD：-40到40°C | ISO11359-2 | 8E-05 cm/cm/°C |
| Thermal Conductivity | ISO8302 | 0.20 W/m/K | |
| Heat Deflection Temperature | 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 105 °C |
| Vicat Softening Temperature | -- | ISO306/B50 | 126 °C |
| Linear thermal expansion coefficient | TD：-40到40°C | ASTME831 | 7E-05 cm/cm/°C |
| Heat Deflection Temperature | 0.45MPa,Unannealed,64.0mmSpan | ISO75-2/Bf | 126 °C |
| Linear thermal expansion coefficient | MD：-40到40°C | ISO11359-2 | 8E-05 cm/cm/°C |
| Heat Deflection Temperature | 1.8MPa,未退火,3.20mm | ASTMD648 | 107 °C |
| Vicat Softening Temperature | ASTMD152510 | 126 °C | |
| -- | ISO306/B120 | 127 °C | |
| Ball PressureTest | 75°C | IEC60695-10-2 | Pass |
| Linear thermal expansion coefficient | MD：-40到40°C | ASTME831 | 7E-05 cm/cm/°C |
| Mechanical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/XCY630 76701 |
|---|---|---|---|
| Flexural Modulus | 50.0mm跨距 | ASTMD790 | 2300 Mpa |
| Tensile Stress | 断裂 | ISO527-2/50 | 53.0 Mpa |
| Tensile Elongation | 断裂 | ASTMD638 | 120 % |
| Tensile Strain | 断裂 | ISO527-2/50 | 120 % |
| Tensile Modulus | ISO527-2/1 | 2250 Mpa | |
| Tensile Strength | 屈服 | ASTMD638 | 54.0 Mpa |
| Flexural Strength | 屈服,50.0mm跨距 | ASTMD790 | 89.0 Mpa |
| Flexural Modulus | ISO178 | 2200 Mpa | |
| Tensile Elongation | 屈服 | ASTMD638 | 4.5 % |
| Tensile Stress | 屈服 | ISO527-2/50 | 54.0 Mpa |
| Tensile Strain | 屈服 | ISO527-2/50 | 4.5 % |
| Flexural Strength | ISO178 | 82.0 Mpa | |
| Tensile Modulus | ASTMD638 | 2300 Mpa | |
| Tensile Strength | 断裂 | ASTMD638 | 53.0 Mpa |
| Physical | Test Condition | Test Method | SABIC INNOVATIVE US/XCY630 76701 |
|---|---|---|---|
| Moisture Absorption | 平衡,23°C,50%RH | ISO62 | 0.15 % |
| Modeling Shrinkage | MD：3.20mm | 内部方法 | 0.50to0.70 % |
| Melt Volume flow Rate | 260°C/5.0kg | ISO1133 | 22.0 cm3/10min |
| Modeling Shrinkage | TD：3.20mm | 内部方法 | 0.50to0.70 % |
| Moisture Absorption | 饱和,23°C | ISO62 | 0.40 % |
| Melt Mass-Flow Rate | 260°C/5.0kg | ASTMD1238 | 26 g/10min |
| Melt Viscosity | 260°C,1500sec^-1 | ISO11443 | 170 Pa·s |
| Impact Properties | Test Condition | Test Method | SABIC INNOVATIVE US/XCY630 76701 |
|---|---|---|---|
| Notched Izod Impact Strength | -30°C | ISO180/1A | 30 kJ/m² |
| Instrumented Dart Impact | -30°C,TotalEnergy | ASTMD3763 | 67.0 J |
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 30 kJ/m² |
| Instrumented Dart Impact | 23°C,TotalEnergy | ASTMD3763 | 55.0 J |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 65 kJ/m² |
| Notched Izod Impact Strength | 23°C | ISO180/1A | 65 kJ/m² |
| Electrical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/XCY630 76701 |
|---|---|---|---|
| Dielectric Strength | 3.20mm,在油中 | IEC60243-1 | 17 KV/mm |
| 1.60mm,在油中 | IEC60243-1 | 25 KV/mm | |
| Volume Resistivity | IEC60093 | >1.0E+15 ohms·cm | |
| Dielectric Strength | 0.800mm,在油中 | IEC60243-1 | 35 KV/mm |
| Surface Resistivity | IEC60093 | >1.0E+15 ohms |