PC
PC SABIC INNOVATIVE US EXL1810T-7R1D047
Injection grade
US$ 4,543 / MT
FOB Guangzhou port, China
injectionTest ConditionTest MethodSABIC INNOVATIVE US/EXL1810T-7R1D047
Back pressure0.300 to 0.700 Mpa
Temperature at the front of the material cylinder295 to 315 °C
Screw speed40 to 70 rpm
Mold temperature70 to 95 °C
Processing (melt) temperature295 to 315 °C
Suggested injection volume40 to 60 %
Suggested maximum moisture content0.020 %
Spray nozzle temperature290 to 310 °C
Exhaust hole depth0.025 to 0.076 mm
drying temperature120 °C
Temperature in the middle of the barrel280 to 305 °C
drying time3.0 to 4.0 hr
Temperature at the rear of the barrel270 to 295 °C
mechanical propertiesTest ConditionTest MethodSABIC INNOVATIVE US/EXL1810T-7R1D047
bending strength--5,6ISO 17892.0 Mpa
Bending modulus50.0 mm Span4ASTM D7902350 Mpa
bending strengthYield, 50.0 mm Span4ASTM D79099.0 Mpa
elongationBreakISO 527-2/50120 %
Yield3ASTM D6385.8 %
YieldISO 527-2/505.4 %
Break3ASTM D638120 %
tensile strengthBreakISO 527-2/5056.0 Mpa
YieldISO 527-2/5059.0 Mpa
Yield3ASTM D63859.0 Mpa
Tensile modulus--2ASTM D6382360 Mpa
--ISO 527-2/12400 Mpa
Bending modulus--5ISO 1782250 Mpa
tensile strengthBreak3ASTM D63858.0 Mpa
optical performanceTest ConditionTest MethodSABIC INNOVATIVE US/EXL1810T-7R1D047
turbidity2540 μmASTM D10033.0 %
transmissivity2540 μmASTM D100382.0 %
Physical propertiesTest ConditionTest MethodSABIC INNOVATIVE US/EXL1810T-7R1D047
Shrinkage rateAcross FlowFlow : 3.20 mmInternal Method0.40 - 0.80 %
Water absorption rateSaturation, 23°CISO 620.12 %
Melt Volume Flow Rate (MVR)300°C/1.2 kgISO 113333.0 cm3/10min
Shrinkage rateFlow : 3.20 mmInternal Method0.40 - 0.80 %
Water absorption rateEquilibrium, 23°C, 50% RHISO 620.090 %
melt mass-flow rate300°C/1.2 kgASTM D123835 g/10 min
flammabilityTest ConditionTest MethodSABIC INNOVATIVE US/EXL1810T-7R1D047
Hot filament ignition temperature3.0 mmIEC 60695-2-13850 °C
Burning wire flammability index3.0 mmIEC 60695-2-12960 °C
Hot filament ignition temperature0.8 mmIEC 60695-2-13825 °C
UL flame retardant rating1.5 mmUL 94HB
Electrical performanceTest ConditionTest MethodSABIC INNOVATIVE US/EXL1810T-7R1D047
Surface resistivityASTM D257> 1.0E+15 ohms
Volume resistivityASTM D257> 1.0E+15 ohms·cm
impact performanceTest ConditionTest MethodSABIC INNOVATIVE US/EXL1810T-7R1D047
Impact strength of simply supported beam without notch-30°CISO 179/1eU无断裂
Suspended wall beam without notch impact strength23°CISO 180/1U无断裂
Charpy Notched Impact Strength-30°CISO 179/1eA40 kJ/m²
Impact strength of simply supported beam without notch23°CISO 179/1eU无断裂
Dart impact23°C, Total EnergyASTM D376379.0 J
Charpy Notched Impact Strength23°CISO 179/1eA65 kJ/m²
Suspended wall beam without notch impact strength-30°CISO 180/1U无断裂
hardnessTest ConditionTest MethodSABIC INNOVATIVE US/EXL1810T-7R1D047
Rockwell hardnessL -SaleISO 2039-290
thermal performanceTest ConditionTest MethodSABIC INNOVATIVE US/EXL1810T-7R1D047
Hot deformation temperature1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span9ISO 75-2/Af117 °C
Linear coefficient of thermal expansionFlow : 23 to 80°CISO 11359-26.5E-5 cm/cm/°C
Vicat softening temperature--ISO 306/B50137 °C
RTI ElecUL 746130 °C
Linear coefficient of thermal expansionAcross Flow : 23 to 80°CISO 11359-27.4E-5 cm/cm/°C
Flow : -40 to 95°CASTM E8316.5E-5 cm/cm/°C
RTIUL 746130 °C
Hot deformation temperature1.8 MPa, Unannealed, 3.20 mmASTM D648120 °C
Vicat softening temperature--ISO 306/B120140 °C
Linear coefficient of thermal expansionAcross Flow : -40 to 95°CASTM E8317.4E-5 cm/cm/°C
Ball Pressure Test123 to 127°CIEC 60695-10-2通过
Vicat softening temperature--ASTM D152510138 °C