Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
TPU C 90 A 13 000 CN BASF SHANGHAI
Elastollan®
tubing,packing,sporting goods
UV resistance,Hydrolysis resistance,Antibacterial
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | BASF SHANGHAI/C 90 A 13 000 CN |
|---|---|---|---|
| Shore hardness | 邵氏A | ASTM D2240 | 90 |
| Mechanical properties | Test Condition | Test Method | BASF SHANGHAI/C 90 A 13 000 CN |
|---|---|---|---|
| Taber abraser | ASTM D1044 | 25.0 mg | |
| wear resistance | DIN 53516 | 25 mm³ | |
| Tensile modulus | 注塑 | ASTM D412 | 39.3 Mpa |
| Flexural modulus | 注塑 | ASTM D790 | 48.3 Mpa |
| elastomer | Test Condition | Test Method | BASF SHANGHAI/C 90 A 13 000 CN |
|---|---|---|---|
| tensile strength | 100%应变 | ASTM D412 | 10.3 Mpa |
| elongation | 断裂 | ASTM D412 | 520 % |
| compression set | 70°C,22hr | ASTM D395B | 40 % |
| tensile strength | ASTM D412 | 44.1 Mpa | |
| 300%应变 | ASTM D412 | 22.8 Mpa | |
| compression set | 23°C,22hr | ASTM D395B | 25 % |
| tear strength | ASTM D624 | 133 kN/m |
| physical property | Test Condition | Test Method | BASF SHANGHAI/C 90 A 13 000 CN |
|---|---|---|---|
| melt mass-flow rate | 210°C/21.6kg | ASTM D1238 | 30to50 g/10min |
| Thermal performance | Test Condition | Test Method | BASF SHANGHAI/C 90 A 13 000 CN |
|---|---|---|---|
| vicat | ASTM D1525 | 128 °C | |
| 内部方法 | 113 °C | ||
| Glass Transition Temperature | 内部方法 | -38.0 °C |