EAA 3003 STYRON US
PRIMACOR™
chip、container、Food packaging
Heat sealing performance、high strength、High toughness、Resistance to stress crac
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Other performance | Test Condition | Test Method | STYRON US/3003 |
|---|---|---|---|
| Starting temperature of heat sealing | Internal Method | ℃ |
| film | Test Condition | Test Method | STYRON US/3003 |
|---|---|---|---|
| Initial sealing temperature | 内部方法 | 90.0 °C |
| Basic performance | Test Condition | Test Method | STYRON US/3003 |
|---|---|---|---|
| melt mass-flow rate | 190℃/2.16kg | ISO 1133 | 7.8 g/10min |
| Monomer content | Internal Method | % | |
| melt mass-flow rate | 190℃/2.16kg | ASTM D-1238 | 7.8 g/10min |
| Mechanical properties | Test Condition | Test Method | STYRON US/3003 |
|---|---|---|---|
| tensile strength | 屈服 | ASTM D-638 | 7.5 MPa |
| Tensile modulus | 2%正割 | ASTMD638 | 130 Mpa |
| elongation | 断裂 | ASTMD638 | 590 % |
| Tensile modulus | 2% Secant | ISO 527-2 | 130 MPa |
| tensile strength | 屈服 | ASTMD638 | 7.50 Mpa |
| 断裂 | ISO 527-2 | 18 MPa | |
| Tensile modulus | 2% Secant | ASTM D-638 | 130 MPa |
| tensile strength | 屈服 | ISO 527-2 | 7.5 MPa |
| 断裂 | ASTMD638 | 18.0 Mpa | |
| elongation at break | ASTM D-638 | 590 % | |
| ISO 527-2 | 590 % | ||
| tensile strength | 断裂 | ASTM D-638 | 18 MPa |
| physical property | Test Condition | Test Method | STYRON US/3003 |
|---|---|---|---|
| Content of comonomer | 内部方法 | 6.5 % | |
| melt mass-flow rate | 190°C/2.16kg | ASTMD1238 | 7.8 g/10min |
| Thermal performance | Test Condition | Test Method | STYRON US/3003 |
|---|---|---|---|
| melting temperature | 内部方法 | 100 °C | |
| Internal Method | ℃ | ||
| vicat | ISO 306/A | 90.0 °C |