PC DX11355-BKNAT SABIC INNOVATIVE NANSHA
LNP™ THERMOCOMP™
Automotive components,Electronic and electrical components
Thermal stability,High mobility
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/DX11355-BKNAT |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C | ASTM D4812 | 2100 J/m |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/DX11355-BKNAT |
|---|---|---|---|
| bending strength | 屈服, 50.0 mm 跨距 | 90 Mpa | |
| Tensile modulus | ASTM D638 | 2600 Mpa | |
| bending strength | 断裂, 50.0 mm 跨距 | 89 Mpa | |
| elongation | 屈服 | 5.4 % | |
| tensile strength | 屈服 | 58 Mpa | |
| 断裂 | 52 Mpa | ||
| elongation | 断裂 | 70 % | |
| Flexural modulus | 50.0 mm 跨距 | ASTM D790 | 2400 Mpa |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/DX11355-BKNAT |
|---|---|---|---|
| relative permittivity | 1.00 GHz | IEC 60250 | 2.92 |
| Dissipation Factor | 1.00 GHz | IEC 60250 | 0.007 |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/DX11355-BKNAT |
|---|---|---|---|
| UL flame retardant rating | 0.60mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/DX11355-BKNAT |
|---|---|---|---|
| Shrinkage rate | 横向流动 : 24小时 | 0.5 % | |
| 流动 : 24小时 | 0.5 % | ||
| Water absorption rate | 24 hr, 23°C, 50% RH | ASTM D570 | 0.01 % |
| melt mass-flow rate | 300°C/1.2 kg | ASTM D1238 | 12 g/10 min |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/DX11355-BKNAT |
|---|---|---|---|
| RTI | UL 746B | 80 °C | |
| Linear coefficient of thermal expansion | 垂直 : -40 到 40°C | 0.000067 cm/cm/°C | |
| 流动 : -40 到 40°C | 0.000062 cm/cm/°C | ||
| RTI Imp | UL 746B | 80 °C | |
| Heat distortion temperature | 1.8 MPa, 未退火, 3.20 mm，HDT | ASTM D648 | 114 °C |
| RTI Elec | UL 746B | 80 °C |
| injection | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/DX11355-BKNAT |
|---|---|---|---|
| screw speed | 40 to 70 rpm | ||
| Suggested maximum moisture content | 0.02 % | ||
| Processing (melt) temperature | 275 to 300 °C | ||
| drying temperature | 100 to 110 °C | ||
| Suggested injection volume | 30 to 80 % | ||
| drying time | 3.0 to 4.0 hr | ||
| Temperature in the middle of the barrel | 255 to 295 °C | ||
| Temperature at the rear of the barrel | 250 to 290 °C | ||
| Exhaust hole depth | 0.038 to 0.076 mm | ||
| Hopper temperature | 60 to 80 °C | ||
| Temperature at the front of the material cylinder | 260 to 300 °C | ||
| Back pressure | 0.300 to 0.700 Mpa | ||
| Temperature | 60 to 90 °C | ||
| Spray nozzle temperature | 275 to 300 °C |