ABS/PA NM-19 INEOS STYRO KOREA
Terblend®N
Automotive sector、Automotive interior parts
High impact resistance、High mobility、Easy to process、UV resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | INEOS STYRO KOREA/NM-19 |
|---|---|---|---|
| Heat Deflection Temperature | 0.45MPa,Annealed | ISO75-2/B | 85.0 °C |
| Linear thermal expansion coefficient | MD | ISO11359-2 | 1E-04 cm/cm/°C |
| Vicat Softening Temperature | -- | ISO306/B50 | 102 °C |
| Heat Deflection Temperature | 1.8MPa,退火 | ISO75-2/A | 65.0 °C |
| Vicat Softening Temperature | -- | ISO306/A50 | 160 °C |
| Hardness | Test Condition | Test Method | INEOS STYRO KOREA/NM-19 |
|---|---|---|---|
| Ball Indentation Hardness | ISO2039-1 | 86.0 Mpa | |
| Rockwell Hardness | R级 | ISO2039-2 | 103 |
| Films Properties | Test Condition | Test Method | INEOS STYRO KOREA/NM-19 |
|---|---|---|---|
| Elongation - MD | 断裂 | ISO527-3 | >50 % |
| Mechanical Properties | Test Condition | Test Method | INEOS STYRO KOREA/NM-19 |
|---|---|---|---|
| Flexural Modulus | ISO178 | 1800 Mpa | |
| Tensile Strain | 屈服,23°C | ISO527-2 | 3.5 % |
| Tensile Stress | 屈服,23°C | ISO527-2 | 43.0 Mpa |
| Flexural Stress | ISO178 | 62.0 Mpa | |
| Tensile Modulus | ISO527-2 | 2000 Mpa |
| Physical | Test Condition | Test Method | INEOS STYRO KOREA/NM-19 |
|---|---|---|---|
| Moisture Absorption | 平衡,23°C,50%RH | ISO62 | 1.2 % |
| Melt Volume flow Rate | 240°C/10.0kg | ISO1133 | 30.0 cm3/10min |
| Modeling Shrinkage | ISO294-4 | 0.80 % |
| Electrical Properties | Test Condition | Test Method | INEOS STYRO KOREA/NM-19 |
|---|---|---|---|
| Volume Resistivity | IEC60093 | >1.0E+15 ohms·cm | |
| Surface Resistivity | IEC60093 | 1E+14 ohms | |
| Relative Permittivity | 1MHz | IEC60250 | 2.90 |
| Dissipation Factor? | 1MHz | IEC60250 | 0.015 |