POM A25-03 MITSUBISHI ENGINEERING JAPAN
Iupital™
Automotive sector、Electronic and Electrical
High rigidity
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/A25-03 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 250 kJ/m² |
| Mechanical properties | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/A25-03 |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 3050 Mpa | |
| Nominal tensile fracture strain | ISO 527-2 | 35 % | |
| bending strength | ISO 178 | 98.0 Mpa | |
| Flexural modulus | ISO 178 | 2950 Mpa | |
| Tensile strain | 屈服 | ISO 527-2 | 11 % |
| tensile strength | 屈服 | ISO 527-2 | 69.0 Mpa |
| Electrical performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/A25-03 |
|---|---|---|---|
| Volume resistivity | IEC 60093 | 1E+14 ohms·cm | |
| Surface Resistivity | IEC 60093 | 1E+16 ohms |
| flammability | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/A25-03 |
|---|---|---|---|
| UL flame retardant rating | 0.8mm | UL 94 | HB |
| physical property | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/A25-03 |
|---|---|---|---|
| Melt volume flow rate | 190°C/2.16kg | ISO 1133 | 12.0 cm3/10min |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.22 % |
| melt mass-flow rate | 190°C/2.16kg | ISO 1133 | 14 g/10min |
| Shrinkage rate | MD：3.00mm | 2.1 % |
| Thermal performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/A25-03 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 170 °C | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 160 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 105 °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 1.1E-04 cm/cm/°C |
| TD | ISO 11359-2 | 1.1E-04 cm/cm/°C |