PC EXL4019-WH8D346 PC vs. - Plastic Material Properties Comparison Chart at Plas.com

Material Selector

All

Plastic Materials Additives Masterbatch Material Selector Price Index Trade Data Plastic News About Us

Material Comparison

Add Comparison Model

Select Products for Comparison (1/4)

Highlight Differences

Hide Same

Product Name / Manufacturer / Model

Grade

Reference Price

PC SABIC INNOVATIVE NANSHA EXL4019-WH8D346

Enhanced level

US$ 3,910 / MT

FOB Guangzhou port, China

injection	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/EXL4019-WH8D346
Back pressure			0.300 to 0.700 Mpa
Temperature at the front of the material cylinder			310 to 330 °C
Spray nozzle temperature			305 to 325 °C
Screw speed			40 to 70 rpm
Mold temperature			80 to 115 °C
Exhaust hole depth			0.025 to 0.076 mm
Processing (melt) temperature			310 to 330 °C
drying temperature			120 °C
Suggested injection volume			40 to 60 %
Temperature in the middle of the barrel			300 to 320 °C
drying time			3.0 to 4.0 hr
Suggested maximum moisture content			0.020 %
Temperature at the rear of the barrel			290 to 310 °C
mechanical properties	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/EXL4019-WH8D346
bending strength	--5,6	ISO 178	98.0 Mpa
elongation	Yield3	ASTM D638	4.3 %
elongation		Break	ISO 527-2/5	8.7 %
Bending modulus	50.0 mm Span4	ASTM D790	3500 Mpa
elongation	Break3	ASTM D638	14 %
bending strength	Yield, 50.0 mm Span4	ASTM D790	103 Mpa
tensile strength	Break	ISO 527-2/5	48.0 Mpa
tensile strength		Yield3	ASTM D638	55.0 Mpa
elongation	Yield	ISO 527-2/5	4.3 %
Tensile modulus	--2	ASTM D638	3950 Mpa
Tensile modulus		--	ISO 527-2/1	3900 Mpa
tensile strength	Yield	ISO 527-2/5	54.0 Mpa
Bending modulus	--5	ISO 178	3450 Mpa
tensile strength	Break3	ASTM D638	45.0 Mpa
impact performance	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/EXL4019-WH8D346
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	15 kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	无断裂
Impact strength of simply supported beam without notch		-30°C	ISO 179/1eU	无断裂
Dart impact	23°C, Total Energy	ASTM D3763	40.0 J
Charpy Notched Impact Strength	23°C	ISO 179/1eA	25 kJ/m²
Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	无断裂
Suspended wall beam without notch impact strength		23°C	ISO 180/1U	无断裂
Physical properties	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/EXL4019-WH8D346
Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	0.40 %
Shrinkage rate	Across FlowFlow : 3.20 mm	Internal Method	0.20 - 0.60 %
Water absorption rate	Saturation, 23°C	ISO 62	0.15 %
melt mass-flow rate	300°C/1.2 kg	ASTM D1238	7.5 g/10 min
Melt Volume Flow Rate (MVR)	300°C/1.2 kg	ISO 1133	6.00 cm3/10min
Shrinkage rate	Flow : 3.20 mm	Internal Method	0.20 - 0.60 %
thermal performance	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/EXL4019-WH8D346
Linear coefficient of thermal expansion	Across Flow : -40 to 40°C	ASTM E831	7.0E-5 cm/cm/°C
Linear coefficient of thermal expansion		Across Flow : -40°C	ISO 11359-2	7.0E-5 cm/cm/°C
Ball Pressure Test	73 to 77°C	IEC 60695-10-2	通过
Hot deformation temperature	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	137 °C
Hot deformation temperature		1.8 MPa, Unannealed, 4.00 mm, 100 mm Span9	ISO 75-2/Ae	135 °C
Vicat softening temperature		ASTM D152510	146 °C
Linear coefficient of thermal expansion	Flow : -40 to 40°C	ASTM E831	4.7E-5 cm/cm/°C
flammability	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/EXL4019-WH8D346
UL flame retardant rating	0.75 mm	UL 94	HB