Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PEEK 450FE20 VICTREX UK
VICTREX®
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | VICTREX UK/450FE20 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 无断裂 |
| Suspended wall beam without notch impact strength | 23°C | ISO 180 | 无断裂 |
| hardness | Test Condition | Test Method | VICTREX UK/450FE20 |
|---|---|---|---|
| Shore hardness | 邵氏D,23°C | ISO 868 | 81 |
| Mechanical properties | Test Condition | Test Method | VICTREX UK/450FE20 |
|---|---|---|---|
| bending strength | 275°C | ISO 178 | 13.0 Mpa |
| 3.5%应变,23°C | ISO 178 | 100 Mpa | |
| Tensile strain | 断裂,23°C | ISO 527-2 | 25 % |
| bending strength | 125°C | ISO 178 | 70.0 Mpa |
| compression stress | 120°C | ISO 604 | 65.0 Mpa |
| tensile strength | 屈服,23°C | ISO 527-2 | 78.0 Mpa |
| Flexural modulus | 23°C | ISO 178 | 3200 Mpa |
| Tensile modulus | 23°C | ISO 527-2 | 3200 Mpa |
| compression stress | 23°C | ISO 604 | 105 Mpa |
| bending strength | 175°C | ISO 178 | 18.0 Mpa |
| 23°C6 | ISO 178 | 125 Mpa |
| Electrical performance | Test Condition | Test Method | VICTREX UK/450FE20 |
|---|---|---|---|
| dielectric constant | 23°C,1kHz | IEC 60250 | 2.80 |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 4 | |
| Volume resistivity | 23°C | IEC 60093 | 1E+16 ohms·cm |
| dielectric strength | 2.00mm | IEC 60243-1 | 26 KV/mm |
| Dissipation Factor | 23°C,1MHz | IEC 60250 | 4E-03 |
| Filling analysis | Test Condition | Test Method | VICTREX UK/450FE20 |
|---|---|---|---|
| melt viscosity | 400°C | ISO 11443 | 350 Pa·s |
| physical property | Test Condition | Test Method | VICTREX UK/450FE20 |
|---|---|---|---|
| Shrinkage rate | TD | ISO 294-4 | 1.7 % |
| MD | ISO 294-4 | 1.2 % | |
| spiral flow length | 内部方法 | 13.0 CM |
| Thermal performance | Test Condition | Test Method | VICTREX UK/450FE20 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/Af | 150 °C |
| melting temperature | ISO 11357-3 | 343 °C | |
| Linear coefficient of thermal expansion | MD:>143°C | ISO 11359-2 | 1.2E-04 cm/cm/°C |
| MD:<143°C | ISO 11359-2 | 4E-05 cm/cm/°C | |
| Glass Transition Temperature | --8 | ISO 11357-2 | 150 °C |
| Linear coefficient of thermal expansion | TD:>143°C | ISO 11359-2 | 1.4E-04 cm/cm/°C |
| Glass Transition Temperature | --7 | ISO 11357-2 | 143 °C |
| Linear coefficient of thermal expansion | TD:<143°C | ISO 11359-2 | 6E-05 cm/cm/°C |