Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PEEK 550GL30 JILIN JOINATURE
ZYPEEK®
Aerospace、Electrical field、Electronic field、Electric wire、Cable、Industrial machinery、Medical supplies、Nursing supplies、Automotive sector
enhance、Moderate liquidity、Glass fiber reinforced
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | JILIN JOINATURE/550GL30 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 有缺口 | ISO 180-A | 10 kJ/m² |
| ISO 180/U | 60 kJ/m² | ||
| Charpy Notched Impact Strength | ISO 179/1eA | 8 kJ/m² | |
| ISO 179/1U | 55 kJ/m² |
| Mechanical properties | Test Condition | Test Method | JILIN JOINATURE/550GL30 |
|---|---|---|---|
| bending strength | 断裂，23℃ | ISO 178 | 265 Mpa |
| Flexural modulus | 23℃ | ISO 178 | 11300 Mpa |
| compressive strength | 23℃ | ISO 604 | 250 Mpa |
| tensile strength | 断裂，23℃ | ISO 527 | 175 Mpa |
| Shore hardness | 23℃ | ISO 868 | 88 D 级 |
| Tensile strain | 断裂，23℃ | ISO 527 | 2.7 % |
| Electrical performance | Test Condition | Test Method | JILIN JOINATURE/550GL30 |
|---|---|---|---|
| dielectric strength | 2 mm | IEC 60243-1 | 25 KV/mm |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 4 | |
| Loss factor | 23℃, 1MHz，正切 | IEC 60250 | 0.005 |
| dielectric constant | 23 ℃, 1 kHz | IEC 60250 | 3.2 |
| Volume resistivity | 23 ℃，1V | IEC 60093 | 10^16 ohms·cm |
| physical property | Test Condition | Test Method | JILIN JOINATURE/550GL30 |
|---|---|---|---|
| density | 结晶 | ISO 1183 | 1.51 g/cm³ |
| Shrinkage rate | TD | ISO 294-4 | 0.3 % |
| MD | ISO 294-4 | 0.8 % | |
| Water absorption rate | 23℃，24hr，3.2 mm厚拉伸棒 | ISO 62-1 | 0.04 % |
| 平衡，23℃，3.20 mm厚拉伸棒 | ISO 62-1 | 0.3 % | |
| melt mass-flow rate | 380℃，5.0kg | ISO 1133 | 6 g/10min |
| Thermal performance | Test Condition | Test Method | JILIN JOINATURE/550GL30 |
|---|---|---|---|
| Heat distortion temperature | 1.8 Mpa，HDT | ISO 75-f | 328 °C |
| Linear coefficient of thermal expansion | 低于Tg沿着流动方向 | ISO 11359 | 18 ppm/K |
| Glass Transition Temperature | 起始 | ISO 11357 | 143 °C |
| melting temperature | ISO 11357 | 343 °C | |
| thermal conductivity | 23℃ | ISO 22007-4 | 0.3 W/m/K |
| specific heat | 23℃ | DSC | 1.7 kJ/kg/℃ |
| Linear coefficient of thermal expansion | 高于Tg沿着流动方向 | ISO 11359 | 18 ppm/K |