Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC/PBT X4820 BK1006 SABIC INNOVATIVE SHANGHAI
XENOY™
Automotive Applications
High mobility、High impact resistance、Dimensional stability
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/X4820 BK1006 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 60 kJ/m² |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 60.0 J |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 15 kJ/m² |
| 23°C | ISO 180/1A | 55 kJ/m² |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/X4820 BK1006 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 3000 Mpa | |
| elongation | 屈服 | ASTM D638 | 4.2 % |
| tensile strength | 断裂 | ASTM D638 | 58.0 Mpa |
| Tensile strain | 屈服 | ISO 527-2/50 | 4.2 % |
| tensile strength | 断裂 | ISO 527-2/50 | 52.0 Mpa |
| Flexural modulus | 50.0mm跨距 | ASTM D790 | 2900 Mpa |
| tensile strength | 屈服 | ISO 527-2/50 | 58.0 Mpa |
| Tensile modulus | ASTM D638 | 3200 Mpa | |
| bending strength | 屈服,50.0mm跨距 | ASTM D790 | 91.0 Mpa |
| elongation | 断裂 | ASTM D638 | 140 % |
| bending strength | ISO 178 | 87.0 Mpa | |
| Flexural modulus | ISO 178 | 2850 Mpa | |
| tensile strength | 屈服 | ASTM D638 | 57.0 Mpa |
| Tensile strain | 断裂 | ISO 527-2/50 | 100 % |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/X4820 BK1006 |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.95-1.1 % |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.14 % |
| 饱和,23°C | ISO 62 | 0.42 % | |
| Melt volume flow rate | 265°C/5.0kg | ISO 1133 | 12.0 cm3/10min |
| melt mass-flow rate | 250°C/5.0kg | ASTM D1238 | 10 g/10min |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/X4820 BK1006 |
|---|---|---|---|
| vicat | -- | ISO 306/B120 | 134 °C |
| Linear coefficient of thermal expansion | TD：-40到40°C | ASTME831 | 1.1E-04 cm/cm/°C |
| TD：-40到40°C | ISO 11359-2 | 1.1E-04 cm/cm/°C | |
| vicat | -- | ISO 306/B50 | 132 °C |
| Linear coefficient of thermal expansion | MD：-40到40°C | ASTME831 | 7.5E-05 cm/cm/°C |
| MD：-40到40°C | ISO 11359-2 | 7.5E-05 cm/cm/°C | |
| Heat distortion temperature | 1.8MPa,Unannealed,64.0mmSpan，HDT | ISO 75-2/Af | 94.0 °C |
| vicat | ASTM D152510 | 130 °C | |
| Heat distortion temperature | 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 98.0 °C |