PC/PBT
PC/PBT SABIC INNOVATIVE SHANGHAI 5220U-7A1D383
Flame retardant grade
US$ 3,000 / MT
FOB Shanghai port, China
mechanical propertiesTest ConditionTest MethodSABIC INNOVATIVE SHANGHAI/5220U-7A1D383
bending strengthISO 17880.0 Mpa
Tensile strainBreakASTM D638120 %
bending strengthYield,50.0mmSpanASTM D79084.0 Mpa
tensile strengthBreakASTM D63851.0 Mpa
Bending modulusISO 1782000 Mpa
Tensile strainYieldISO 527-2/504.0 %
Bending modulus50.0mmSpanASTM D7902030 Mpa
Tensile modulusISO 527-2/12050 Mpa
tensile strengthBreakISO 527-2/5050.0 Mpa
Tensile strainYieldASTM D6384.0 %
tensile strengthYieldISO 527-2/5050.0 Mpa
Tensile modulus--3ASTM D6382250 Mpa
Tensile strainBreakISO 527-2/50120 %
Tensile modulus--4ASTM D6382250 Mpa
tensile strengthYieldASTM D63853.0 Mpa
Physical propertiesTest ConditionTest MethodSABIC INNOVATIVE SHANGHAI/5220U-7A1D383
densityISO 11831.22 g/cm³
melt mass-flow rate250°C/5.0kgISO 113316 g/10min
Shrinkage rateTD2Internal Method0.80-1.0 %
Specific volumeASTM D7920.830 cm³/g
Outdoor applicabilityUL 746Cf2
Melt Volume Flow Rate (MVR)250°C/5.0kgISO 113315.0 cm3/10min
densityASTM D7921.21 g/cm³
Water absorption rateEquilibrium,23°C,50%RHISO 620.15 %
Shrinkage rateMD：3.20mmInternal Method0.80-1.0 %
Water absorption rateSaturation,23°CISO 620.50 %
impact performanceTest ConditionTest MethodSABIC INNOVATIVE SHANGHAI/5220U-7A1D383
Impact strength of cantilever beam gap-40°CASTM D256300 J/m
-30°CASTM D256530 J/m
23°CASTM D256710 J/m
23°CISO 180/1A50 kJ/m²
Charpy Notched Impact Strength23°CISO 179/1eA55 kJ/m²
Dart impact23°C,TotalEnergyASTM D376360.0 J
Impact strength of cantilever beam gap-30°CISO 180/1A30 kJ/m²
thermal performanceTest ConditionTest MethodSABIC INNOVATIVE SHANGHAI/5220U-7A1D383
Linear coefficient of thermal expansionTD：-40to40°CASTME8319E-05 cm/cm/°C
RTI StrUL 74675.0 °C
Linear coefficient of thermal expansionTD：-40to40°CISO 11359-29E-05 cm/cm/°C
Vicat softening temperature--ISO 306/B50120 °C
Hot deformation temperature1.8MPa,Unannealed,64.0mmSpanISO 75-2/Af75.0 °C
1.8MPa,Unannealed,3.20mmASTM D64884.0 °C
1.8MPa,Unannealed,6.40mmASTM D64899.0 °C
Linear coefficient of thermal expansionMD：-40to40°CISO 11359-29.5E-05 cm/cm/°C
Hot deformation temperature0.45MPa,Unannealed,6.40mmASTM D648107 °C
Linear coefficient of thermal expansionMD：-40to40°CASTME8319.5E-05 cm/cm/°C
RTI ElecUL 74675.0 °C
RTI ImpUL 74675.0 °C
Vicat softening temperature--ISO 306/B120125 °C
ASTM D152512122 °C
Electrical performanceTest ConditionTest MethodSABIC INNOVATIVE SHANGHAI/5220U-7A1D383
Hot wire ignitionHWIUL 746PLC 3
Compared to the anti leakage trace indexCTIUL 746PLC 1
High arc combustion indexHAIUL 746PLC 0
High voltage arc tracing rateHVTRUL 746PLC 0
Arc resistanceASTM D495PLC 5
flammabilityTest ConditionTest MethodSABIC INNOVATIVE SHANGHAI/5220U-7A1D383
UL flame retardant rating1.5mmUL 94HB

Supplier Join

Contact Us

Get App

Top

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index

+86 0755 27873515

Room 906, Global Digital Building, No. 9 Gaoxin Middle 3rd Road, Maling Community, Yuehai Subdistrict, Nanshan District, Shenzhen, Guangdong Province, China