PPA UC008H-BKNAT SABIC INNOVATIVE US
LNP™ THERMOCOMP™ 
Mechanical parts、consumer goods
Thermal stability、Carbon fiber reinforced
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodSABIC INNOVATIVE US/UC008H-BKNAT
Suspended wall beam without notch impact strength23°CISO 180/1U45 kJ/m²
Multi axis Instrumented Impact EnergyISO 6603-25.00 J
Impact strength of cantilever beam gap23°CISO 180/1A7.3 kJ/m²
Dart impact23°C,EnergyatPeakLoadASTM D37637.00 J
Mechanical propertiesTest ConditionTest MethodSABIC INNOVATIVE US/UC008H-BKNAT
Tensile modulusISO 527-2/135500 Mpa
ASTM D63833800 Mpa
elongation断裂ASTM D6381.0 %
bending strengthISO 178425 Mpa
Tensile strain断裂ISO 527-21.3 %
Flexural modulusISO 17826600 Mpa
bending strengthASTM D790441 Mpa
tensile strength 断裂ASTM D638261 Mpa
断裂ISO 527-2232 Mpa
Flexural modulusASTM D79026800 Mpa
Electrical performanceTest ConditionTest MethodSABIC INNOVATIVE US/UC008H-BKNAT
Volume resistivityASTM D2571.0E+2to1.0E+4 ohms·cm
Surface ResistivityASTM D2571.0E+2to1.0E+4 ohms
physical property Test ConditionTest MethodSABIC INNOVATIVE US/UC008H-BKNAT
Shrinkage rateMD:24小时ISO 294-40.70-0.90 %
MD：24小时ASTM D9550.70-0.90 %
Water absorption rate24hr,50%RHASTM D5700.40 %
平衡,23°C,50%RHISO 620.46to1.4 %
Shrinkage rateTD：24hrASTM D9550.70-0.90 %
TD:24小时ISO 294-40.70-0.90 %
Thermal performanceTest ConditionTest MethodSABIC INNOVATIVE US/UC008H-BKNAT
Heat distortion temperature1.8MPa,未退火,64.0mm跨距，HDTISO 75-2/Af>250 °C
1.8MPa,未退火,3.20mm，HDTASTM D648>249 °C