Material Comparison

Product Info

Product Name

Brand Name

Usages

Properties

Certificates

PC/ABS CX7240-7T2A6747 SABIC INNOVATIVE SHANGHAI

CYCOLOY™

Architectural application field,Outdoor applications,Nursing supplies,Plastic bag,Casters,Aerospace Applications,Liquid handling,Electrical field,Electronic field,Engine hood parts,Medical supplies

Flame retardant,High impact resistance,High mobility

Plastic Datasheets

thermal performance	Test Condition	Test Method	SABIC INNOVATIVE SHANGHAI/CX7240-7T2A6747
Ball Pressure Test	73 to 77°C	IEC 60695-10-2	通过
Hot deformation temperature	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	100 °C
		1.8 MPa, Unannealed, 3.20 mm	ASTM D648	89.0 °C
		1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span10	ISO 75-2/Af	93.0 °C
		1.8 MPa, Unannealed, 6.40 mm	ASTM D648	99.0 °C
Linear coefficient of thermal expansion	Across Flow : -40°C	ISO 11359-2	7.5E-5 cm/cm/°C
		Flow : -40 to 40°C	ASTM E831	7.5E-5 cm/cm/°C
		Across Flow : -40 to 40°C	ASTM E831	7.5E-5 cm/cm/°C
RTI		UL 746	90.0 °C
RTI Elec		UL 746	90.0 °C
RTI Imp		UL 746	90.0 °C
thermal conductivity		ISO 8302	0.20 W/m/K
Vicat softening temperature	--	ISO 306/B120	113 °C
Vicat softening temperature		--	ASTM D152511	110 °C

mechanical properties	Test Condition	Test Method	SABIC INNOVATIVE SHANGHAI/CX7240-7T2A6747
Bending modulus	--5	ISO 178	2500 Mpa
Bending modulus		50.0 mm Span4	ASTM D790	2500 Mpa
bending strength	Yield, 50.0 mm Span4	ASTM D790	104 Mpa
bending strength		--5,6	ISO 178	96.0 Mpa
elongation	Yield	ISO 527-2/50	4.0 %
		Yield3	ASTM D638	4.1 %
		Break3	ASTM D638	100 %
		Break	ISO 527-2/50	90 %
Tensile modulus	--2	ASTM D638	2600 Mpa
Tensile modulus		--	ISO 527-2/1	2600 Mpa
tensile strength	Yield	ISO 527-2/50	65.0 Mpa
		Break	ISO 527-2/50	50.0 Mpa
		Break3	ASTM D638	58.0 Mpa
		Yield3	ASTM D638	65.0 Mpa

Electrical performance	Test Condition	Test Method	SABIC INNOVATIVE SHANGHAI/CX7240-7T2A6747
Compared to the anti leakage trace index		UL 746	PLC 3
Dielectric strength	0.800 mm, in Oil	IEC 60243-1	35 KV/mm
		1.60 mm, in Oil	IEC 60243-1	25 KV/mm
		3.20 mm, in Oil	IEC 60243-1	17 KV/mm
High arc combustion index		UL 746	PLC 0
Hot wire ignition		UL 746	PLC 3
Surface resistivity		IEC 60093	> 1.0E+15 ohms
Volume resistivity		IEC 60093	> 1.0E+15 ohms·cm

Physical properties	Test Condition	Test Method	SABIC INNOVATIVE SHANGHAI/CX7240-7T2A6747
melt mass-flow rate	260°C/2.16 kg	ASTM D1238	18 g/10 min
Melt Volume Flow Rate (MVR)	260°C/2.16 kg	ISO 1133	15.0 cm3/10min
Shrinkage rate	3.20 mm，Flow	Internal Method	0.40 - 0.60 %
Water absorption rate	Saturation, 23°C	ISO 62	0.20 %
Water absorption rate		Equilibrium, 23°C, 50% RH	ISO 62	0.10 %

impact performance	Test Condition	Test Method	SABIC INNOVATIVE SHANGHAI/CX7240-7T2A6747
Dart impact	23°C, Total Energy	ASTM D3763	65.0 J

flammability	Test Condition	Test Method	SABIC INNOVATIVE SHANGHAI/CX7240-7T2A6747
Burning wire flammability index	0.75 mm	IEC 60695-2-12	960 °C
Burning wire flammability index		0.75 mm13	IEC 60695-2-12	960 °C
Extreme Oxygen Index		ISO 4589-2	34 %
Hot filament ignition temperature	1.5 mm13	IEC 60695-2-13	775 °C
		3.0 mm	IEC 60695-2-13	800 °C
		1.0 mm	IEC 60695-2-13	825 °C
		0.75 mm13	IEC 60695-2-13	775 °C
		3.0 mm13	IEC 60695-2-13	775 °C
UL flame retardant rating	3.0 mm	UL 94	5VA
		0.60 mm	UL 94	V-1
		0.75 mm	UL 94	V-0
		1.5 mm	UL 94	5VB

injection	Test Condition	Test Method	SABIC INNOVATIVE SHANGHAI/CX7240-7T2A6747
drying temperature			80 to 90 °C
drying time			2.0 to 4.0 hr
Exhaust hole depth			0.030 to 0.075 mm
Hopper temperature			60 to 80 °C
Mold temperature			60 to 85 °C
Processing (melt) temperature			250 to 300 °C
Spray nozzle temperature			250 to 300 °C
Suggested maximum moisture content			0.020 %
Temperature at the front of the material cylinder			250 to 300 °C
Temperature at the rear of the barrel			230 to 280 °C
Temperature in the middle of the barrel			240 to 290 °C