Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPA HTNFR52G30BL BK337 DUPONT JAPAN
Zytel®
Automotive interior equip、building materials、Profile
enhance、Glass fiber reinforced、High temperature resistan、Aging resistance、Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | DUPONT JAPAN/HTNFR52G30BL BK337 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 45 kJ/m² |
| -30°C | ISO 179/1eU | 40 kJ/m² |
| Supplementary Information | Test Condition | Test Method | DUPONT JAPAN/HTNFR52G30BL BK337 |
|---|---|---|---|
| Odor | VDA270 | 3.50 |
| Electrical performance | Test Condition | Test Method | DUPONT JAPAN/HTNFR52G30BL BK337 |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 0 | |
| dielectric strength | IEC 60243-1 | 36 KV/mm | |
| Volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
| relative permittivity | 100Hz | IEC 60250 | 4.10 |
| Dissipation Factor | 100Hz | IEC 60250 | 6.5E-03 |
| relative permittivity | 1MHz | IEC 60250 | 3.90 |
| Dissipation Factor | 1MHz | IEC 60250 | 0.012 |
| Mechanical properties | Test Condition | Test Method | DUPONT JAPAN/HTNFR52G30BL BK337 |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 10500 Mpa | |
| bending strength | ISO 178 | 230 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 2.2 % |
| Flexural modulus | ISO 178 | 9000 Mpa | |
| tensile strength | 断裂 | ISO 527-2 | 150 Mpa |
| flammability | Test Condition | Test Method | DUPONT JAPAN/HTNFR52G30BL BK337 |
|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL 94 | V-0 |
| 0.75mm | IEC 60695-11-10,-20 | V-0 | |
| 1.5mm | IEC 60695-11-10,-20 | V-0 | |
| Hot filament ignition temperature | 3.0mm | IEC 60695-2-13 | 800 °C |
| FMVSS flammability | FMVSS302 | DNI | |
| Hot filament ignition temperature | 0.40mm | IEC 60695-2-13 | 700 °C |
| UL flame retardant rating | 1.5mm | UL 94 | V-0 |
| Limiting Oxygen Index | ISO 4589-2 | 37 % | |
| Hot filament ignition temperature | 0.75mm | IEC 60695-2-13 | 725 °C |
| physical property | Test Condition | Test Method | DUPONT JAPAN/HTNFR52G30BL BK337 |
|---|---|---|---|
| Shrinkage rate | TD | ISO 294-4 | 1.0 % |
| MD | ISO 294-4 | 0.30 % |
| Thermal performance | Test Condition | Test Method | DUPONT JAPAN/HTNFR52G30BL BK337 |
|---|---|---|---|
| Linear coefficient of thermal expansion | MD：55to160°C | ISO 11359-2 | 2E-05 cm/cm/°C |
| TD：-- | ISO 11359-2 | 6E-05 cm/cm/°C | |
| melting temperature | ISO 11357-3 | 310 °C | |
| Linear coefficient of thermal expansion | MD：-40to23°C | ISO 11359-2 | 2E-05 cm/cm/°C |
| TD：-40to23°C | ISO 11359-2 | 6E-05 cm/cm/°C | |
| MD：-- | ISO 11359-2 | 2E-05 cm/cm/°C | |
| TD：55to160°C | ISO 11359-2 | 1E-04 cm/cm/°C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 283 °C |
| RTI Elec | 1.5mm | UL 746 | 140 °C |
| 0.40mm | UL 746 | 140 °C | |
| 3.0mm | UL 746 | 140 °C | |
| 0.75mm | UL 746 | 140 °C |