PC EXL9330 GY4D167 SABIC INNOVATIVE THAILAND
LEXAN™ 
Casters、Thin walled products、food
Flame retardant、Toughening、UV resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodSABIC INNOVATIVE THAILAND/EXL9330 GY4D167
The impact strength of a simply supported beam without a notch is 723°CISO 179/1eU无断裂
Dart impact equipped with measuring instruments23°C, Total EnergyASTM D376352.0 J
Impact strength of simply supported beam gap 7-30°CISO 179/1eA60 kJ/m²
The impact strength of a simply supported beam without a notch is 7-30°CISO 179/1eU无断裂
Unnotched Izod Impact Strength-30°CISO 180/1U无断裂
Impact strength of simply supported beam gap 723°CISO 179/1eA75 kJ/m²
Unnotched Izod Impact Strength23°CISO 180/1U无断裂
hardnessTest ConditionTest MethodSABIC INNOVATIVE THAILAND/EXL9330 GY4D167
Ball Indentation HardnessH 358/30ISO 2039-190.0 Mpa
Mechanical propertiesTest ConditionTest MethodSABIC INNOVATIVE THAILAND/EXL9330 GY4D167
tensile strength屈服ISO 527-2/5055.0 Mpa
Bending stress-- 5, 6ISO 17885.0 Mpa
elongation断裂ISO 527-2/50130 %
Flexural modulus-- 5ISO 1782200 Mpa
elongation屈服 3ASTM D6386.0 %
Bending stress屈服, 50.0 mm 跨距 4ASTM D79088.0 Mpa
Tensile modulus-- 2ASTM D6382100 Mpa
tensile strength屈服 3ASTM D63858.0 Mpa
断裂ISO 527-2/5060.0 Mpa
elongation屈服ISO 527-2/506.0 %
Flexural modulus50.0 mm 跨距 4ASTM D7902060 Mpa
Tensile modulus--ISO 527-2/12100 Mpa
elongation断裂 3ASTM D638130 %
tensile strength断裂 3ASTM D63861.0 Mpa
Electrical performanceTest ConditionTest MethodSABIC INNOVATIVE THAILAND/EXL9330 GY4D167
dielectric constant50 HzIEC 602502.60
Dissipation Factor50 HzASTM D1502.4E-3
dielectric constant1 MHzASTM D1502.90
Dissipation Factor50 HzIEC 602501.0E-3
Compared to the Leakage Tracking Index (CTI)UL 746PLC 3
High arc combustion index (HAI)UL 746PLC 0
CTIIEC 60112225 V
dielectric strength3.20 mm, in OilASTM D14917 KV/mm
dielectric constant60 HzIEC 602502.60
Volume resistivityIEC 60093> 1.0E+15 ohms·cm
dielectric constant60 HzASTM D1502.95
Dissipation Factor60 HzASTM D1502.4E-3
1 MHzASTM D150, IEC 602508.5E-3
60 HzIEC 602501.0E-3
Hot wire ignition (HWI)UL 746PLC 1
Surface ResistivityIEC 60093> 1.0E+15 ohms
dielectric strength3.20 mm, 在油中IEC 60243-116 KV/mm
dielectric constant50 kHzASTM D1502.95
1 MHzIEC 602502.70
flammabilityTest ConditionTest MethodSABIC INNOVATIVE THAILAND/EXL9330 GY4D167
UL flame retardant rating3.0 mmUL 945VA
Hot filament ignition temperature1.0 mmIEC 60695-2-13825 °C
UL flame retardant rating1.5 mmUL 94V-0
Burning wire flammability index1.0 mmIEC 60695-2-12960 °C
Limiting Oxygen IndexISO 4589-235 %
physical property Test ConditionTest MethodSABIC INNOVATIVE THAILAND/EXL9330 GY4D167
Water absorption rate平衡, 23°C, 50% RHISO 620.15 %
Shrinkage rate横向流动 : 3.20 mm内部方法0.40 到 0.80 %
Outdoor applicabilityUL 746Cf1
density--ASTM D7921.18 g/cm³
Molten Volume Flow Rate (MVR)300°C/1.2 kgISO 11339.00 cm3/10min
melt mass-flow rate300°C/1.2 kgASTM D123810 g/10 min
density--ISO 11831.19 g/cm³
Shrinkage rate流动 : 3.20 mm内部方法0.40 到 0.80 %
Water absorption rate饱和, 23°CISO 620.35 %
Thermal performanceTest ConditionTest MethodSABIC INNOVATIVE THAILAND/EXL9330 GY4D167
Linear thermal expansion coefficient流动 : 23 到 80°CISO 11359-27.2E-5 cm/cm/°C
Thermal deformation temperature under load0.45 MPa, 未退火, 4.00 mm, 100 mm 跨距 11ISO 75-2/Be135 °C
Linear thermal expansion coefficient流动 : -40 到 40°CASTM E8316.7E-5 cm/cm/°C
Thermal deformation temperature under load0.45 MPa, 未退火, 3.20 mmASTM D648134 °C
1.8 MPa, 未退火, 6.40 mmASTM D648124 °C
1.8 MPa, 未退火, 4.00 mm, 100 mm 跨距 11ISO 75-2/Ae124 °C
RTIUL 746125 °C
vicat--ASTM D152512, ISO 306/B12012142 °C
Linear thermal expansion coefficient横向 : 23 到 80°CISO 11359-27.7E-5 cm/cm/°C
横向 : -40 到 40°CASTM E8316.7E-5 cm/cm/°C
Thermal deformation temperature under load1.8 MPa, 未退火, 3.20 mmASTM D648120 °C
Ball Pressure Test123 到 127°CIEC 60695-10-2通过
vicat--ISO 306/B50140 °C
RTI ImpUL 746115 °C
RTI ElecUL 746125 °C
injectionTest ConditionTest MethodSABIC INNOVATIVE THAILAND/EXL9330 GY4D167
Nozzle Temperature290 到 310 °C
Processing (melt) temperature295 到 315 °C
drying temperature120 °C
Exhaust hole depth0.025 到 0.076 mm
Temperature at the front of the material cylinder295 到 315 °C
Suggested maximum moisture content0.020 %
Temperature in the middle of the barrel280 到 305 °C
Temperature70 到 95 °C
screw speed40 到 70 rpm
Temperature at the rear of the barrel215 到 295 °C
Back pressure0.300 到 0.700 Mpa
drying time3.0 到 4.0 hr
Suggested injection volume40 到 60 %