Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC/ABS HM-1100 K21294 Samsung Cheil South Korea
INFINO®
Electronic and Electrical、TV
Glass fiber reinforced、Flame retardant、Filler: Glass fiber reinf
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Samsung Cheil South Korea/HM-1100 K21294 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 7.0 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 8.0 kJ/m² |
| hardness | Test Condition | Test Method | Samsung Cheil South Korea/HM-1100 K21294 |
|---|---|---|---|
| Rockwell hardness | R级 | ISO 2039-2 | 118 |
| R级 | ASTM D785 | 118 |
| Mechanical properties | Test Condition | Test Method | Samsung Cheil South Korea/HM-1100 K21294 |
|---|---|---|---|
| tensile strength | 屈服 | ISO 527-2/5 | 55.0 Mpa |
| Tensile modulus | ASTM D638 | 3400 Mpa | |
| tensile strength | 断裂 | ISO 527-2/5 | 55.0 Mpa |
| elongation | 断裂 | ASTM D638 | 4.0 % |
| bending strength | ISO 178 | 95.0 Mpa | |
| Flexural modulus | ISO 178 | 3800 Mpa | |
| bending strength | ASTM D790 | 96.0 Mpa | |
| Tensile strain | 断裂 | ISO 527-2/5 | 4.0 % |
| Tensile modulus | ISO 527-2/5 | 3400 Mpa | |
| tensile strength | 断裂 | ASTM D638 | 59.0 Mpa |
| 屈服 | ASTM D638 | 59.0 Mpa | |
| Flexural modulus | ASTM D790 | 3900 Mpa |
| flammability | Test Condition | Test Method | Samsung Cheil South Korea/HM-1100 K21294 |
|---|---|---|---|
| UL flame retardant rating | 3.0mm | UL 94 | V-0 |
| 2.0mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | Samsung Cheil South Korea/HM-1100 K21294 |
|---|---|---|---|
| Shrinkage rate | TD | ISO 2577 | 0.10 % |
| melt mass-flow rate | 250°C/2.16kg | ASTM D1238 | 7.0 g/10min |
| 250°C/2.16kg | ISO 1133 | 7.0 g/10min | |
| ash content | -- | ASTM D5630 | 9.5 % |
| Shrinkage rate | MD：3.20mm | ASTM D955 | 0.10 % |
| ash content | -- | ISO 3451 | 9.5 % |
| Tg(halfwidth)-DSC | 101 °C | ||
| Shrinkage rate | TD | ASTM D955 | 0.10 % |
| melt mass-flow rate | 220°C/10.0kg | ASTM D1238 | 22 g/10min |
| Shrinkage rate | MD:3.20mm | ISO 2577 | 0.10 % |
| melt mass-flow rate | 220°C/10.0kg | ISO 1133 | 22 g/10min |
| Thermal performance | Test Condition | Test Method | Samsung Cheil South Korea/HM-1100 K21294 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,Unannealed,4.00mm，HDT | ISO 75-2/A | 96.0 °C |
| 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 96.0 °C | |
| 0.45MPa,Unannealed,4.00mm，HDT | ISO 75-2/B | 97.0 °C | |
| 1.8MPa,Annealed,4.00mm，HDT | ISO 75-2/A | 98.0 °C | |
| vicat | ISO 306/B50 | 99.0 °C | |
| Heat distortion temperature | 0.45MPa,未退火,6.40mm，HDT | ASTM D648 | 97.0 °C |
| 0.45MPa,Annealed,4.00mm，HDT | ISO 75-2/B | 102 °C |