PC/PBT 6620-BK1066 SABIC INNOVATIVE US
XENOY™
Automotive Applications、Casters、Plastic bag
Glass fiber reinforced、Low warpage
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/6620-BK1066 |
|---|---|---|---|
| Dart impact | 23°C4 | ASTM D3029 | 54.2 J |
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 900 J/m |
| -30°C | ASTM D256 | 670 J/m | |
| 23°C | ASTM D4812 | 1600 J/m | |
| Dart impact | 23°C | ASTM D3029 | 54.2 J |
| hardness | Test Condition | Test Method | SABIC INNOVATIVE US/6620-BK1066 |
|---|---|---|---|
| Rockwell hardness | R级 | ASTM D785 | 108 |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE US/6620-BK1066 |
|---|---|---|---|
| Volume resistivity | ASTM D257 | 5.5E+16 ohms·cm | |
| Dissipation Factor | 100Hz | ASTM D150 | 2E-03 |
| 1MHz | ASTM D150 | 0.020 | |
| dielectric constant | 100kHz | ASTM D150 | 3.00 |
| High arc combustion index (HAI) | HAI | UL 746 | PLC 0 |
| Dissipation Factor | 100kHz | ASTM D150 | 0.020 |
| dielectric strength | 3.20mm,在油中 | ASTM D149 | 19 KV/mm |
| dielectric constant | 1MHz | ASTM D150 | 3.00 |
| 100Hz | ASTM D150 | 3.10 | |
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL 746 | PLC 1 |
| Hot wire ignition (HWI) | HWI | UL 746 | PLC 3 |
| arc resistance | ASTM D495 | PLC 5 | |
| dielectric strength | 3.20mm,inAir | ASTM D149 | 19 KV/mm |
| 1.60mm,在油中 | ASTM D149 | 28 KV/mm | |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 0 |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/6620-BK1066 |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 180 % |
| bending strength | 屈服,50.0mm跨距 | ASTM D790 | 64.1 Mpa |
| tensile strength | 屈服 | ASTM D638 | 43.4 Mpa |
| Flexural modulus | 50.0mm跨距 | ASTM D790 | 1720 Mpa |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE US/6620-BK1066 |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/6620-BK1066 |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 1.6-1.8 % |
| Water absorption rate | 24hr | ASTM D570 | 0.080 % |
| Shrinkage rate | TD：3.20mm | 内部方法 | 1.6-1.8 % |
| density | ASTM D792 | 1.20 g/cm³ | |
| Specific volume | ASTM D792 | 0.838 cm³/g |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/6620-BK1066 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 60.0 °C |
| Linear coefficient of thermal expansion | TD：-40到40°C | ASTME831 | 9.8E-05 cm/cm/°C |
| MD：60to138°C | ASTME831 | 1E-04 cm/cm/°C | |
| Heat distortion temperature | 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 93.0 °C |
| Linear coefficient of thermal expansion | MD：-40to40°C | ASTME831 | 9.4E-05 cm/cm/°C |
| RTI Imp | UL 746 | 75.0 °C | |
| Heat distortion temperature | 0.45MPa,未退火,6.40mm，HDT | ASTM D648 | 98.9 °C |
| RTI Str | UL 746 | 75.0 °C | |
| Heat distortion temperature | 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 53.0 °C |
| RTI Elec | UL 746 | 75.0 °C |