ABS POLYLAN T-17H POLYMA Kunststoff GmbH & Co. KG
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | POLYMA Kunststoff GmbH & Co. KG/POLYLAN T-17H |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C,6.35mm | ASTM D256 | 200 J/m |
| hardness | Test Condition | Test Method | POLYMA Kunststoff GmbH & Co. KG/POLYLAN T-17H |
|---|---|---|---|
| Rockwell hardness | R级,23°C | ASTM D785 | 110 |
| R计秤,23°C | ISO 2039-2 | 110 |
| Mechanical properties | Test Condition | Test Method | POLYMA Kunststoff GmbH & Co. KG/POLYLAN T-17H |
|---|---|---|---|
| bending strength | 23°C | ASTMD790 | 84.0 MPa |
| Tensile modulus | 23°C | ASTMD638 | 2650 MPa |
| tensile strength | 屈服,23°C | ASTMD638 | 50.0 MPa |
| flammability | Test Condition | Test Method | POLYMA Kunststoff GmbH & Co. KG/POLYLAN T-17H |
|---|---|---|---|
| UL flame retardant rating | 1.6mm | UL 94 | HB |
| physical property | Test Condition | Test Method | POLYMA Kunststoff GmbH & Co. KG/POLYLAN T-17H |
|---|---|---|---|
| melt mass-flow rate | 200°C/5.0kg | ASTMD1238 | 1.6 g/10min |
| 200°C/10.0kg | ASTMD1238 | 17 g/10min | |
| density | ISO 1183 | 1.05 g/cm³ |
| Thermal performance | Test Condition | Test Method | POLYMA Kunststoff GmbH & Co. KG/POLYLAN T-17H |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,退火,12.7mm，HDT | ASTM D648 | 101 °C |
| 1.8MPa,未退火,12.7mm，HDT | ASTM D648 | 89.0 °C | |
| 1.8MPa,退火，HDT | ISO 75-2/A | 101 °C | |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 89.0 °C | |
| vicat | ISO 306/A | 104 °C |