Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
POM 3510 ASAHI JAPAN
TENAC™-C
Automotive Applications
high viscosity、High temperature resistan、High gloss、High impact resistance、High rigidity、wear resistant、High mobility、UV resistance、high strength、Thermal stability
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | ASAHI JAPAN/3510 |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D256/ISO 179 | 78 kg·cm/cm(J/M)ft·lb/in | |
| bending strength | ASTM D790/ISO 178 | 88 kg/cm²(MPa)[Lb/in²] | |
| Flexural modulus | ASTM D790/ISO 178 | 2600 kg/cm²(MPa)[Lb/in²] | |
| elongation | ASTM D638/ISO 527 | 75 % | |
| Rockwell hardness | ASTM D785 | 78 | |
| tensile strength | ASTM D638/ISO 527 | 61 kg/cm²(MPa)[Lb/in²] |
| other | Test Condition | Test Method | ASAHI JAPAN/3510 |
|---|---|---|---|
| characteristic | 挤出等级 | ||
| purpose | 汽车部件.齿轮.控制杆等。 |
| Physical properties | Test Condition | Test Method | ASAHI JAPAN/3510 |
|---|---|---|---|
| Shrinkage rate | ASTM D955 | 1.6-2.0 % | |
| density | ASTM D792/ISO 1183 | 1.41 | |
| melt mass-flow rate | ASTM D1238/ISO 1133 | 2.8 g/10min | |
| Water absorption rate | ASTM D570/ISO 62 | 0.2 % |
| Thermal performance | Test Condition | Test Method | ASAHI JAPAN/3510 |
|---|---|---|---|
| Heat distortion temperature | HDT | ASTM D648/ISO 75 | 110 ℃（℉） |