PS HK HIPS SRG100 Hong Kong Petrochemical Co. Ltd.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Hong Kong Petrochemical Co. Ltd./HK HIPS SRG100 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C,3.20mm | ASTM D256 | 130 J/m |
| hardness | Test Condition | Test Method | Hong Kong Petrochemical Co. Ltd./HK HIPS SRG100 |
|---|---|---|---|
| Rockwell hardness | L计秤 | ASTM D785 | 72 |
| Mechanical properties | Test Condition | Test Method | Hong Kong Petrochemical Co. Ltd./HK HIPS SRG100 |
|---|---|---|---|
| elongation | 断裂,3.20mm | ASTM D638 | 58 % |
| bending strength | 3.20mm | ASTM D790 | 52.0 MPa |
| tensile strength | 3.20mm | ASTM D638 | 23.0 MPa |
| Tensile modulus | 3.20mm | ASTM D638 | 2000 MPa |
| Flexural modulus | 3.20mm | ASTM D790 | 2100 MPa |
| tensile strength | 屈服,3.20mm | ASTM D638 | 30.0 MPa |
| optical performance | Test Condition | Test Method | Hong Kong Petrochemical Co. Ltd./HK HIPS SRG100 |
|---|---|---|---|
| gloss | 60° | ASTM D523 | 98 |
| flammability | Test Condition | Test Method | Hong Kong Petrochemical Co. Ltd./HK HIPS SRG100 |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB |
| physical property | Test Condition | Test Method | Hong Kong Petrochemical Co. Ltd./HK HIPS SRG100 |
|---|---|---|---|
| melt mass-flow rate | 200°C/5.0kg | ASTM D1238 | 3.5 g/10min |
| Apparent density | ASTM D1895 | 0.65 g/cm³ | |
| density | ASTM D792 | 1.04 g/cm³ |
| Thermal performance | Test Condition | Test Method | Hong Kong Petrochemical Co. Ltd./HK HIPS SRG100 |
|---|---|---|---|
| vicat | -- | ASTM D15255 | 96.0 °C |
| Heat distortion temperature | 1.8MPa,未退火,12.7mm，HDT | ASTM D648 | 90.0 °C |
| vicat | -- | ASTM D15254 | 103 °C |