PA6 A1030GFL UNICAR JAPAN

UNITIKA

Engine hood parts,Automotive sector,Construction field,Application in the automotive field,Parts under the hood of a car,Electrical enclosure,Architectural application field,Vehicle electronics

Glass fiber reinforced,Filler: Glass fabric rein,30% filler by weight

Plastic Datasheets

hardness	Test Condition	Test Method	UNICAR JAPAN/A1030GFL
Rockwell hardness	R-Sale		120 107

thermal performance	Test Condition	Test Method	UNICAR JAPAN/A1030GFL
Hot deformation temperature	0.45MPa,Unannealed	°C	217 --
Hot deformation temperature		1.8MPa,Unannealed	°C	203 --
Linear coefficient of thermal expansion	MD	cm/cm/°C	3.1E-05 3.1E-05

mechanical properties	Test Condition	Test Method	UNICAR JAPAN/A1030GFL
Bending modulus		MPa	8200 5000
bending strength		MPa	250 160
Tensile modulus		MPa	9600 6000
Tensile strain	Break	%	3.1 5.3
tensile strength	Break		170 MPa

Electrical performance	Test Condition	Test Method	UNICAR JAPAN/A1030GFL
Compared to the anti leakage trace index		V	550
Dielectric constant	1MHz		3.30 3.60
Dielectric strength	1.00mm	kV/mm	42
Dissipation factor	1MHz		0.022 0.12
Volume resistivity		ohms·cm	2E+15 7E+13

Physical properties	Test Condition	Test Method	UNICAR JAPAN/A1030GFL
Shrinkage rate	TD:3.20mm	%	0.70 0.70
Shrinkage rate		MD:3.20mm	%	0.20 0.20
Water absorption rate	23°C,24hr	%	1.3 1.3
Water absorption rate		Equilibrium,23°C,50%RH	%	2.0 2.0

impact performance	Test Condition	Test Method	UNICAR JAPAN/A1030GFL
Impact strength of simply supported beam without notch		kJ/m²	70 85

flammability	Test Condition	Test Method	UNICAR JAPAN/A1030GFL
UL flame retardant rating	0.75mm		HB HB