ABS TA-15W BK UMG JAPAN
UMG ABS®
--
High rigidity,High impact resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | UMG JAPAN/TA-15W BK |
|---|---|---|---|
| Tensile stress | 23 ℃，屈服 | ISO 527-2 | 59 Mpa |
| bending strength | 23 ℃ | ISO 178 | 99 Mpa |
| Flexural modulus | 23 ℃ | ISO 178 | 2750 Mpa |
| Tensile modulus | 23 ℃ | ISO 527-2 | 2300 Mpa |
| Charpy Notched Impact Strength | 23 ℃ | ISO 179 | 45 kJ/m² |
| physical property | Test Condition | Test Method | UMG JAPAN/TA-15W BK |
|---|---|---|---|
| Rockwell hardness | ISO 2039-2 | 113 Mpa | |
| Melt volume flow rate | 230℃/2.16kg | ISO 1133 | 11 cm3/10min |
| density | ISO 1183 | 1.12 g/cm³ | |
| Shrinkage rate | 流量 | ISO 294-4 | 0.5-0.7 % |
| Thermal performance | Test Condition | Test Method | UMG JAPAN/TA-15W BK |
|---|---|---|---|
| Obstructive property | 1.50mm | UL 94 | HB |
| Linear coefficient of thermal expansion | ISO 11359-2 | 0.000090 cm/cm/℃ | |
| Heat distortion temperature | 1.8MPa，HDT | ISO 75-2/A | 97 °C |