Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA46 TE341 DSM HOLAND
Stanyl®
Casters、Automotive Applications
Electrical performance
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | DSM HOLAND/TE341 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 10 kJ/m² |
| -30°C | ISO 179/1eA | 4.0 kJ/m² | |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 10 kJ/m² |
| -40°C | ISO 180/1A | 4.0 kJ/m² | |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 无断裂 |
| 23°C | ISO 179/1eU | 无断裂 |
| Mechanical properties | Test Condition | Test Method | DSM HOLAND/TE341 |
|---|---|---|---|
| Tensile stress | 屈服, 120°C | ISO 527-2 | 50.0 Mpa |
| Tensile modulus | -- | ISO 527-2 | 3300 Mpa |
| Tensile stress | 屈服 | ISO 527-2 | 100 Mpa |
| 屈服, 200°C | ISO 527-2 | 30.0 Mpa | |
| Flexural modulus | -- | ISO 178 | 3000 Mpa |
| Tensile modulus | 180°C | ISO 527-2 | 600 Mpa |
| 160°C | ISO 527-2 | 650 Mpa | |
| Nominal tensile fracture strain | 200°C | ISO 527-2 | > 50 % |
| Tensile modulus | 120°C | ISO 527-2 | 800 Mpa |
| Flexural modulus | 160°C | ISO 178 | 600 Mpa |
| Tensile modulus | 200°C | ISO 527-2 | 500 Mpa |
| Nominal tensile fracture strain | -- | ISO 527-2 | 40 % |
| Flexural modulus | 120°C | ISO 178 | 800 Mpa |
| Tensile stress | 屈服, 180°C | ISO 527-2 | 35.0 Mpa |
| 屈服, 160°C | ISO 527-2 | 40.0 Mpa | |
| Nominal tensile fracture strain | 120°C | ISO 527-2 | > 50 % |
| 180°C | ISO 527-2 | > 50 % | |
| 160°C | ISO 527-2 | > 50 % |
| Electrical performance | Test Condition | Test Method | DSM HOLAND/TE341 |
|---|---|---|---|
| CTI | IEC 60112 | 600 V | |
| dielectric strength | IEC 60243-1 | 25 KV/mm | |
| 100 Hz | IEC 60250 | 4.00 | |
| Volume resistivity | IEC 60093 | 1.0E+15 ohms·cm | |
| 1 MHz | IEC 60250 | 3.60 |
| flammability | Test Condition | Test Method | DSM HOLAND/TE341 |
|---|---|---|---|
| Flammability level | 0.75 mm | IEC 60695-11-10, -20 | V-2 |
| 1.5 mm | IEC 60695-11-10, -20 | V-2 |
| physical property | Test Condition | Test Method | DSM HOLAND/TE341 |
|---|---|---|---|
| Water absorption rate | 平衡, 23°C, 50% RH | ISO 62 | 3.7 % |
| density | ISO 1183 | 1.18 g/cm³ | |
| Shrinkage rate | 流量 | ISO 294-4 | 2.0 % |
| 横向流量 | ISO 294-4 | 2.0 % |
| Thermal performance | Test Condition | Test Method | DSM HOLAND/TE341 |
|---|---|---|---|
| 流动 | ISO 11359-2 | 8.5E-5 cm/cm/°C | |
| 横向 | ISO 11359-2 | 1.1E-4 cm/cm/°C | |
| RTI Elec | 0.75 mm | UL 746 | 130 °C |
| Heat distortion temperature | 0.45 MPa, 未退火 | ISO 75-2/B | 280 °C |
| 1.8 MPa, 未退火 | ISO 75-2/A | 190 °C | |
| Thermal Index - 5000 hr | IEC 60216 | 128 °C | |
| Melting temperature 3 | ISO 11357-3 | 295 °C |