AES SE20 UMG JAPAN
DIALAC®
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
hardness | Test Condition | Test Method | UMG JAPAN/SE20 |
---|---|---|---|
Rockwell hardness | ISO 2039-2 | 107 R |
Mechanical properties | Test Condition | Test Method | UMG JAPAN/SE20 |
---|---|---|---|
bending strength | 23°C | ISO 178 | 76 Mpa |
Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 5.0 kJ/m² |
23°C | ISO 179/1eA | 13 kJ/m² | |
tensile strength | 23℃ | ISO 527-2 | 47.0 Mpa |
Flexural modulus | 23℃ | ISO 178 | 2600 Mpa |
Charpy Notched Impact Strength | -30℃ | ISO 179 | 5.0 kJ/m² |
Flexural modulus | 23°C | ISO 178 | 2600 Mpa |
Tensile modulus | 23°C | ISO 527-2 | 2350 Mpa |
Rockwell hardness | 23℃ | ISO 2039-2 | 107 R 计秤 |
Tensile modulus | 23℃ | ISO 527-2 | 2350 Mpa |
tensile strength | 23°C | ISO 527-2 | 47 Mpa |
bending strength | 23℃ | ISO 178 | 76.0 Mpa |
Electrical performance | Test Condition | Test Method | UMG JAPAN/SE20 |
---|---|---|---|
dielectric strength | IEC 60243-1 | 32 KV/mm | |
Volume resistivity | IEC 60093 | 1E+15 Ω.cm |
flammability | Test Condition | Test Method | UMG JAPAN/SE20 |
---|---|---|---|
UL flame retardant rating | UL -94 | HB 1.50mm | |
UL -94 | HB 3.00mm |
physical property | Test Condition | Test Method | UMG JAPAN/SE20 |
---|---|---|---|
melt mass-flow rate | 220℃/10Kg | ISO 1133 | 11.00 cm3/10min |
Shrinkage rate | MD2.0mm | ISO 294-4 | 0.70 % |
MD,23℃ | ISO 294-4 | 0.60 - 0.80 % | |
Melt volume flow rate | 220℃/2.16 kg | ISO 1133 | 11.0 cm3/10min |
Thermal performance | Test Condition | Test Method | UMG JAPAN/SE20 |
---|---|---|---|
Linear coefficient of thermal expansion | 流动 | ISO 11359-2 | 0.000090 cm/cm/℃ |
Heat distortion temperature | 1.80MPa退火,HDT | ISO 75-2/Af | 82 °C |
1.80MPa,未退火,HDT | ISO 75-2/Af | 82.0 °C | |
Linear coefficient of thermal expansion | MD | ISO 11359-2 | 9E-05 cm/cm/°C |
UL flame retardant rating | 1.50mm | UL 94 | HB |