PC ML0992-BK1A068 SABIC INNOVATIVE NANSHA
LEXAN™
--
Middle flow、Low temperature and high 、Short molding cycle
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE NANSHA/ML0992-BK1A068
Melt Volume-Flow Rate (MVR)
300°C/1.2 kg
ISO 1133
cm3/10min
1
Melt mass flow rate
300°C/1.2 kg
ASTM D1238
g/10 min
1
Shrinkage rate
流动 : 3.20 mm
内部方法
%
0
Shrinkage rate
横向流动 : 3.20 mm
内部方法
%
0
Water absorption rate
平衡, 23°C, 50% RH
ISO 62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE NANSHA/ML0992-BK1A068
Tensile modulus
ASTM D638
Mpa
2
tensile strength
屈服
ASTM D638
Mpa
5
tensile strength
断裂
ASTM D638
Mpa
5
elongation
屈服
ASTM D638
%
5
elongation
断裂
ASTM D638
%
8
Bending modulus
50.0 mm 跨距
ASTM D790
Mpa
2
bending strength
屈服, 50.0 mm 跨距
ASTM D790
Mpa
8
Thermal performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE NANSHA/ML0992-BK1A068
Hot deformation temperature
1.8 MPa, 未退火, 3.20 mm
ASTM D648
°C
1