PC LUVOCOM® 50/TF/15/NAT LEHVOSS Group
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | LEHVOSS Group/LUVOCOM® 50/TF/15/NAT |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 120 kJ/m² |
| Mechanical properties | Test Condition | Test Method | LEHVOSS Group/LUVOCOM® 50/TF/15/NAT |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 2700 MPa | |
| tensile strength | 断裂 | ISO 527-2 | 55.0 MPa |
| Tensile strain | 屈服 | ISO 527-2 | 5.0 % |
| Bending Strain | ISO 178 | 6.5 % | |
| Flexural modulus | ISO 178 | 2200 MPa | |
| bending strength | ISO 178 | 75.0 MPa |
| Electrical performance | Test Condition | Test Method | LEHVOSS Group/LUVOCOM® 50/TF/15/NAT |
|---|---|---|---|
| insulation resistance | IEC 60167 | >1.0E+12 ohms |
| flammability | Test Condition | Test Method | LEHVOSS Group/LUVOCOM® 50/TF/15/NAT |
|---|---|---|---|
| UL flame retardant rating | UL 94 | V-0 |
| physical property | Test Condition | Test Method | LEHVOSS Group/LUVOCOM® 50/TF/15/NAT |
|---|---|---|---|
| Melt volume flow rate | 300°C/5.0kg | ISO 1133 | 50.0 cm³/10min |
| Shrinkage rate | DIN 16901 | 0.60to0.80 % | |
| melt mass-flow rate | 300°C/5.0kg | ISO 1133 | 55 g/10min |
| Water absorption rate | 23°C,24hr | <0.20 % | |
| density | ISO 1183 | 1.30 g/cm³ |
| Thermal performance | Test Condition | Test Method | LEHVOSS Group/LUVOCOM® 50/TF/15/NAT |
|---|---|---|---|
| thermal conductivity | DIN 52612 | 0.20 W/m/K | |
| Continuous use temperature | UL 746B | 130 °C | |
| vicat | ISO 306/A | 160 °C | |
| Linear coefficient of thermal expansion | MD | DIN 53752 | 7E-05 cm/cm/°C |
| maximum service temperature | ShortTerm | 150 °C |