PBT 5010GNH5 BK MITSUBISHI ENGINEERING JAPAN
NOVADURAN™
Bottle cap、Fitness equipment、Automotive sector、Electronic field、Electrical field
Glass fiber reinforced、Filler: Glass fiber reinf、30%、Filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/5010GNH5 BK |
---|---|---|---|
Impact strength of simply supported beam without notch | 23°C | ISO 179 | 45 kJ/m² |
Electrical performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/5010GNH5 BK |
---|---|---|---|
dielectric strength | 1.00mm | IEC 60243-1 | 24 KV/mm |
Volume resistivity | IEC 60093 | 5E+16 ohms·cm | |
relative permittivity | 1MHz | IEC 60250 | 3.90 |
Surface Resistivity | IEC 60093 | 6E+15 ohms | |
Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 3 |
Dissipation Factor | 1MHz | IEC 60250 | 0.014 |
Mechanical properties | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/5010GNH5 BK |
---|---|---|---|
Tensile modulus | ISO 527-2 | 11000 Mpa | |
bending strength | ISO 178 | 210 Mpa | |
Tensile strain | 断裂 | ISO 527-2 | 2.0 % |
Flexural modulus | ISO 178 | 10500 Mpa | |
tensile strength | 断裂 | ISO 527-2 | 135 Mpa |
flammability | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/5010GNH5 BK |
---|---|---|---|
UL flame retardant rating | 0.8mm | UL 94 | V-0 |
physical property | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/5010GNH5 BK |
---|---|---|---|
Shrinkage rate | MD:2.00mm | 0.40 % | |
吸水率(饱和,23°C) | 0.070 % | ||
TD:2.00mm | 1.1 % |
Thermal performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/5010GNH5 BK |
---|---|---|---|
melting temperature | ISO 11357-3 | 224 °C | |
Linear coefficient of thermal expansion | MD:-30to120°C | ISO 11359-2 | 2E-05 cm/cm/°C |
MD:50to120°C | ISO 11359-2 | 2E-05 cm/cm/°C | |
TD:-30to120°C | ISO 11359-2 | 1.1E-04 cm/cm/°C | |
MD:-30to50°C | ISO 11359-2 | 2E-05 cm/cm/°C | |
Heat distortion temperature | 0.45MPa,未退火,HDT | ISO 75-2/B | >220 °C |
Linear coefficient of thermal expansion | TD:50to120°C | ISO 11359-2 | 1.4E-04 cm/cm/°C |
TD:-30to50°C | ISO 11359-2 | 7E-05 cm/cm/°C | |
Heat distortion temperature | 1.8MPa,未退火,HDT | ISO 75-2/A | 208 °C |