PES E1010G9-BK10112 BASF GERMANY
--
--
Filler: Glass fiber reinf、45% filler by weight、45% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | BASF GERMANY/E1010G9-BK10112 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 8.0 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 40 kJ/m² |
| Mechanical properties | Test Condition | Test Method | BASF GERMANY/E1010G9-BK10112 |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 15500 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 1.3 % |
| tensile strength | 断裂 | ISO 527-2 | 145 Mpa |
| Electrical performance | Test Condition | Test Method | BASF GERMANY/E1010G9-BK10112 |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | 解决方案A | IEC 60112 | V |
| physical property | Test Condition | Test Method | BASF GERMANY/E1010G9-BK10112 |
|---|---|---|---|
| Apparent density | 0.70to0.80 g/cm³ | ||
| Melt volume flow rate | 360°C/10.0kg | ISO 1133 | 35.0 cm3/10min |
| Shrinkage rate | TD | ISO 294-4 | 0.70 % |
| MD | ISO 294-4 | 0.40 % | |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.65 % |
| density | ISO 1183 | 1.73 g/cm³ |
| Thermal performance | Test Condition | Test Method | BASF GERMANY/E1010G9-BK10112 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 216 °C |
| Linear coefficient of thermal expansion | MD：23到80°C | ISO 11359-2 | 1.3E-05 cm/cm/°C |
| MD：180°C | DIN 53752 | 1.5E-05 cm/cm/°C |