Material Comparison

Product Info
Product Name
Brand Name
Usages
Properties
Certificates
TPV 4175N TEKNOR APEX BELGIUM
SARLINK® 
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

hardnessTest ConditionTest MethodTEKNOR APEX BELGIUM/4175N
Shore hardness邵氏 A, 5 秒, 注塑ASTM D224075
邵氏 A, 5 秒, 挤塑ASTM D224072
Supplementary InformationTest ConditionTest MethodTEKNOR APEX BELGIUM/4175N
Apparent Shear Viscosity - Capillary @ 206/s200°CASTM D3835340 Pa·s
200°CISO 11443340 Pa·s
flammabilityTest ConditionTest MethodTEKNOR APEX BELGIUM/4175N
UL flame retardant rating1.00 mmUL 94HB
squeeze outTest ConditionTest MethodTEKNOR APEX BELGIUM/4175N
Melt Temperature195 to 215 °C
pull roll20.0 to 50.0 °C
die temperature195 to 215 °C
Temperature in Zone 2 of the material cylinder180 to 205 °C
Temperature in Zone 4 of the material cylinder187 to 210 °C
Temperature in Zone 3 of the material cylinder187 to 210 °C
Temperature in Zone 1 of the material cylinder180 to 200 °C
elastomerTest ConditionTest MethodTEKNOR APEX BELGIUM/4175N
elongation横向流量 : 断裂ASTM D412590 %
tear strength--1，横向ISO 34-139 kN/m
compression set70°C, 22 hrASTM D39531 %
tensile strength 流量 : 100%应变ASTM D4125.3 Mpa
横向流量 : 100%应变ASTM D4123.3 Mpa
横向流量 : 断裂ASTM D4128.5 Mpa
流量 : 断裂ASTM D4127.2 Mpa
elongation流量 : 断裂ASTM D412300 %
tear strength-横向ASTM D62439 kN/m
compression set125°C, 70 hrASTM D39545 %
23°C, 22 hrASTM D39522 %
agingTest ConditionTest MethodTEKNOR APEX BELGIUM/4175N
Change rate of tensile strength in air100% 应变 150°C, 168 hr，横向ISO 1883 %
Tensile stress variation during fracture in air - transverse flow rate150°C, 168 hr2.45-16 %
Change rate of tensile strength in air150°C, 168 hr，横向ISO 188-9 %
100% 应变 150°C, 1000 hr，横向2.455 %
Change rate of hardness (Shore) in the air支撐 A, 150°C, 168 hr2.45 3
volume change125°C, 70 hr, 在 IRM 903 油中ASTM D47178 %
Change rate of tensile strength in air135°C, 1000 hr，横向ISO 188-2 %
Tensile stress variation during fracture in air - transverse flow rate135°C, 1000 hr2.45-5 %
Change rate of hardness (Shore) in the air支撐 A, 135°C, 1000 hr2.45 2
Thermal performanceTest ConditionTest MethodTEKNOR APEX BELGIUM/4175N
RTI ImpUL 74665 °C
RTIUL 746100 °C
RTI ElecUL 746100 °C
injectionTest ConditionTest MethodTEKNOR APEX BELGIUM/4175N
screw speed100 to 200 rpm
Temperature in the middle of the barrel180 to 215 °C
Temperature at the rear of the barrel180 to 215 °C
Processing (melt) temperature185 to 220 °C
Temperature at the front of the material cylinder180 to 215 °C
Back pressure0.100 to 1.00 Mpa
Temperature10.0 to 55.0 °C
Spray nozzle temperature187 to 220 °C