Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC GS2030MR2 MITSUBISHI ENGINEERING JAPAN
IUPILON™
Fiber grade
Flame retardant,enhance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| thermal performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/GS2030MR2 |
|---|---|---|---|
| Linear coefficient of thermal expansion | ASTM D696/ISO 11359 | 1.8E-05 mm/mm.℃ |
| Electrical performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/GS2030MR2 |
|---|---|---|---|
| Surface Resistivity | ASTM D257/IEC 60093 | 2E+15 Ω | |
| volume resistivity | ASTM D257/IEC 60093 | 2E+14 Ω.cm | |
| dielectric constant | ASTM D150/IEC 60250 | 3.5 |
| Mechanical properties | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/GS2030MR2 |
|---|---|---|---|
| bending strength | ASTM D790/ISO 178 | 180 kg/cm²(MPa)[Lb/in²] | |
| Elongation at break | ASTM D638/ISO 527 | 2.5 % | |
| Tensile modulus | ASTM D638/ISO 527 | 8900 kg/cm²(MPa)[Lb/in²] | |
| flexural modulus | ASTM D790/ISO 178 | 8500 kg/cm²(MPa)[Lb/in²] |
| Physical properties | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/GS2030MR2 |
|---|---|---|---|
| shrinkage rate | ASTM D955 | 0.05 - 0.25 % | |
| density | ASTM D792/ISO 1183 | 1.43 |
| processability | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/GS2030MR2 |
|---|---|---|---|
| process temperature | 280-300 °C | ||
| mold temperature | 80-120 °C | ||
| Dry conditions | 热风干燥 120℃---約4-8小时 | ||
| screw speed | 50-100 rpm |