PC Iupilon® LSH2010 Mitsubishi Chemical Corporation
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodMitsubishi Chemical Corporation/Iupilon® LSH2010
Charpy Notched Impact Strength23°CISO 17914 kJ/m²
Impact strength of simply supported beam without notch23°CISO 179NoBreak
Mechanical propertiesTest ConditionTest MethodMitsubishi Chemical Corporation/Iupilon® LSH2010
Nominal tensile fracture strainISO 527-2100 %
Tensile modulusISO 527-22500 MPa
Tensile strain屈服ISO 527-26.7 %
tensile strength 屈服ISO 527-257.0 MPa
Flexural modulusISO 1782300 MPa
bending strengthISO 17890.0 MPa
Electrical performanceTest ConditionTest MethodMitsubishi Chemical Corporation/Iupilon® LSH2010
Compared to the Leakage Tracking Index (CTI)CTIUL 746PLC 4
flammabilityTest ConditionTest MethodMitsubishi Chemical Corporation/Iupilon® LSH2010
UL flame retardant rating0.40mmUL 94HB
physical property Test ConditionTest MethodMitsubishi Chemical Corporation/Iupilon® LSH2010
Shrinkage rateTD:3.20mm0.50to0.70 %
吸水率(饱和,23°C)0.13 %
Melt volume flow rate300°C/1.2kgISO 11339.70 cm³/10min
Shrinkage rateMD:3.20mm0.50to0.70 %
densityISO 11831.23 g/cm³
melt mass-flow rate300°C/1.2kgISO 113310 g/10min
Thermal performanceTest ConditionTest MethodMitsubishi Chemical Corporation/Iupilon® LSH2010
Heat distortion temperature0.45MPa,未退火，HDTISO 75-2/B142 °C
1.8MPa,未退火，HDTISO 75-2/A127 °C
Linear coefficient of thermal expansionMDISO 11359-26.4E-05 cm/cm/°C
TDISO 11359-26.8E-05 cm/cm/°C