PA6 H35ZI HONEYWELL USA
Aegis®
--
Low viscosity、High rigidity、high strength、wear resistant、Antichemical、heat-resisting
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | HONEYWELL USA/H35ZI |
|---|---|---|---|
| Rockwell hardness | R级 | ASTMD785 | 119 |
| Mechanical properties | Test Condition | Test Method | HONEYWELL USA/H35ZI |
|---|---|---|---|
| Flexural modulus | 23°C | ASTMD790 | 2470 Mpa |
| Tensile modulus | 23°C | ASTMD638 | 2750 Mpa |
| elongation | 屈服,23°C | ASTMD638 | 4.1 % |
| tensile strength | 屈服,23°C | ASTMD638 | 79.0 Mpa |
| elongation | 断裂,23°C | ASTMD638 | 75 % |
| bending strength | 23°C | ASTMD790 | 96.0 Mpa |
| physical property | Test Condition | Test Method | HONEYWELL USA/H35ZI |
|---|---|---|---|
| ASTMD789 | 33.0到39.0 | ||
| melt mass-flow rate | 235°C/1.0kg | ASTMD1238 | 23 g/10min |
| Shrinkage rate | MD | ASTMD955 | 1.3 % |
| Water absorption rate | 24hr | ASTMD570 | 1.6 % |
| water content | ASTMD6869 | <0.10 % | |
| Water absorption rate | 饱和 | ASTMD570 | 9.5 % |
| 平衡,50%RH | ASTMD570 | 2.7 % | |
| Relative viscosity - @ 96% SAV | 2.34 |
| Thermal performance | Test Condition | Test Method | HONEYWELL USA/H35ZI |
|---|---|---|---|
| MD | ASTME831 | 7.2E-05 cm/cm/°C | |
| Heat distortion temperature | 0.45MPa,未退火 | ASTMD648 | 152 °C |
| 熔融温度 | ASTMD648 | 222 °C | |
| 1.8MPa,未退火 | ASTMD648 | 47.0 °C |