Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA6 8333G BASF GERMANY
Ultramid®
Laptop case、Engine parts
High impact resistance、Oil resistant
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | BASF GERMANY/8333G |
|---|---|---|---|
| Impact strength of cantilever beam gap | -40°C | ISO 180/1A | 14 kJ/m² |
| bending strength | 23°C | ISO 178 | 215 Mpa |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 10 kJ/m² |
| 23°C | ISO 179/1eA | 20 kJ/m² | |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 21 kJ/m² |
| Flexural modulus | 23°C | ISO 178 | 7200 Mpa |
| Tensile modulus | 23°C | ISO 527-2 | 9300 Mpa |
| -40°C | ISO 527-2 | 9200 Mpa | |
| elongation at break | 23°C | ISO 527-2 | 3.5 % |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 78 kJ/m² |
| tensile strength | 23°C | ISO 527-2 | 145 Mpa |
| Electrical performance | Test Condition | Test Method | BASF GERMANY/8333G |
|---|---|---|---|
| Dissipation Factor | 相对漏电起痕指数 | IEC 60112 | 600 V |
| dielectric strength | IEC 60243-1 | 11 KV/mm | |
| dielectric constant | 23°C | IEC 60250 | 3.40 1MHz |
| Dissipation Factor | 23°C | IEC 60250 | 0.010 1MHz |
| dielectric constant | 23°C | IEC 60250 | 3.60 100HZ |
| Dissipation Factor | 23°C | IEC 60250 | 0.010 100HZ |
| Volume resistivity | IEC 60093 | 1E+10 Ω.cm |
| Flame retardant performance | Test Condition | Test Method | BASF GERMANY/8333G |
|---|---|---|---|
| GWIT | 3.00mm | IEC 60695-2-12 | 750 °C |
| Relative temperature of heating wire | 3.00mm | IEC 60695-2-13 | 960 °C |
| UL flame retardant rating | UL -94 | HB 0.80mm | |
| UL -94 | HB 1.50mm | ||
| UL -94 | HB 3.00mm |
| physical property | Test Condition | Test Method | BASF GERMANY/8333G |
|---|---|---|---|
| Water absorption rate | (23°C,24hr) | ISO 62 | 0.90 % |
| (23°C,50RH) | ISO 62 | 1.50 % |
| Thermal performance | Test Condition | Test Method | BASF GERMANY/8333G |
|---|---|---|---|
| Heat distortion temperature | 1.80MPa退火，HDT | ISO 75-2/Af | 205 °C |
| vicat | 熔融温度 | ISO 11357-3 | 220 °C |
| Heat distortion temperature | 0.45MPa未退火，HDT | ISO 75-2/Bf | 220 °C |