Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
LCP E6007LHF SUMITOMO JAPAN
SUMIKASUPER®
Automotive sector
Low warpage、Good forming performance、Glass fiber reinforced、enhance
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
LCP/SUMITOMO JAPAN/E6007LHF
Shrinkage rate
横向流量
内部方法
%
0
Shrinkage rate
流量
内部方法
%
0
Water absorption rate
饱和
ASTM D570
%
0
Water absorption rate 23 ℃/24h
ASTM D570/ISO 62
%
0
Mechanical performance
Test Condition
Test Method
Unit
LCP/SUMITOMO JAPAN/E6007LHF
tensile strength
ASTM D638
Mpa
1
elongation
断裂
ASTM D638
%
5
Bending modulus
23°C
ASTM D790
Mpa
1
Bending modulus
ASTM D790/ISO 178
kg/cm²(MPa)[Lb/in²]
1
bending strength
ASTM D790/ISO 178
kg/cm²(MPa)[Lb/in²]
1
bending strength
23°C
ASTM D790
Mpa
1
Non notched cantilever beam impact
6.40 mm
ASTM D256
J/m
2
Tensile elongation at break (elongation at break)
ASTM D638/ISO 527
%
5
Thermal performance
Test Condition
Test Method
Unit
LCP/SUMITOMO JAPAN/E6007LHF
Hot deformation temperature
ASTM D648/ISO 75
℃（℉）
2
Hot deformation temperature
1.8 MPa, 未退火
ASTM D648
°C
2
Linear coefficient of thermal expansion
流动 : 150°C
内部方法
cm/cm/°C
2
Linear coefficient of thermal expansion
横向 : 150°C
内部方法
cm/cm/°C
8
Electrical performance
Test Condition
Test Method
Unit
LCP/SUMITOMO JAPAN/E6007LHF
Leakage Trace Index
IEC 60112
V
1
Arc resistance
ASTM D495
sec
1
Volume resistivity
ASTM D257
ohms·cm
1
flammability
Test Condition
Test Method
Unit
LCP/SUMITOMO JAPAN/E6007LHF
Soldering Resistance
内部方法
°C
3
Extreme Oxygen Index
ISO 527-1,-2(JIS K7161,7162)
%
4