AES RAMSHINE PVS701 POLYRAM ISRAEL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | POLYRAM ISRAEL/RAMSHINE PVS701 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 240 J/m |
| 23°C | ISO 180 | 17 kJ/m² |
| hardness | Test Condition | Test Method | POLYRAM ISRAEL/RAMSHINE PVS701 |
|---|---|---|---|
| Rockwell hardness | R级 | ISO 2039-2 | 112 |
| R级 | ASTM D785 | 112 |
| Mechanical properties | Test Condition | Test Method | POLYRAM ISRAEL/RAMSHINE PVS701 |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 12 % |
| Tensile strain | 断裂 | ISO 527-2 | 12 % |
| Flexural modulus | ASTM D790 | 2000 MPa | |
| Tensile modulus | ASTM D638 | 2400 MPa | |
| ISO 527-2 | 2400 MPa | ||
| tensile strength | 屈服 | ISO 527-2 | 50.0 MPa |
| 屈服 | ASTM D638 | 50.0 MPa | |
| Flexural modulus | ISO 178 | 2000 MPa | |
| bending strength | ASTM D790 | 70.0 MPa | |
| ISO 178 | 70.0 MPa |
| flammability | Test Condition | Test Method | POLYRAM ISRAEL/RAMSHINE PVS701 |
|---|---|---|---|
| Burning wire flammability index | IEC 60695-2-12 | 550 °C |
| physical property | Test Condition | Test Method | POLYRAM ISRAEL/RAMSHINE PVS701 |
|---|---|---|---|
| Shrinkage rate | ISO 2577 | 0.50 % | |
| MD | ASTM D955 | 0.50 % | |
| density | ASTM D792 | 1.04 g/cm³ | |
| ISO 1183 | 1.04 g/cm³ | ||
| melt mass-flow rate | 220°C/10.0kg | ASTM D1238 | 11 g/10min |
| 220°C/10.0kg | ISO 1133 | 11 g/10min |
| Thermal performance | Test Condition | Test Method | POLYRAM ISRAEL/RAMSHINE PVS701 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 89.0 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 89.0 °C |