PC LDS 3764/23715 MITSUBISHI ENGINEERING JAPAN
IUPILON™
Phone,Laser beacon,Laser direct molding
High mobility
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/LDS 3764/23715 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 无断裂 |
| 23°C | ISO 179/1eU | 无断裂 |
| Electrical performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/LDS 3764/23715 |
|---|---|---|---|
| Volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
| Dissipation Factor | 1.00GHz | IEC 60250 | 5E-03 |
| Surface Resistivity | IEC 60093 | >1.0E+15 ohms | |
| relative permittivity | 1.00GHz | IEC 60250 | 3.00 |
| Mechanical properties | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/LDS 3764/23715 |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 2500 Mpa | |
| Nominal tensile fracture strain | ISO 527-2 | >50 % | |
| bending strength | ISO 178 | 90.0 Mpa | |
| Flexural modulus | ISO 178 | 2400 Mpa | |
| Tensile strain | 屈服 | ISO 527-2 | 5.0 % |
| tensile strength | 屈服 | ISO 527-2 | 60.0 Mpa |
| flammability | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/LDS 3764/23715 |
|---|---|---|---|
| Flammability level | 1.5mm | IEC 60695-11-10,-20 | V-0 |
| 1.0mm | IEC 60695-11-10,-20 | V-1 |
| physical property | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/LDS 3764/23715 |
|---|---|---|---|
| Shrinkage rate | MD | ISO 294-4 | 0.60 % |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.35 % |
| Melt volume flow rate | 260°C/5.0kg | ISO 1133 | 26.0 cm3/10min |
| Thermal performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/LDS 3764/23715 |
|---|---|---|---|
| vicat | ISO 306/B50 | 110 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 104 °C |