Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 CM3004G30 BK TORAY SHENZHEN
Amilan®
Office supplies,Automotive sector,building materials,Electronic field,Electrical field
Flame retardant,Glass fiber reinforced, Glass fiber reinforced b,Filler: Glass fiber reinf,Flame retardant grade,30%,Filler by weight,halogen-containing ,Flame retardant grade,30% filler by weight,halogen-containing
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Other performance | Test Condition | Test Method | TORAY SHENZHEN/CM3004G30 BK |
|---|---|---|---|
| filler content | 1.3%水｜- wt% |
| Impact resistance | Test Condition | Test Method | TORAY SHENZHEN/CM3004G30 BK |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | kJ/m² | 65 70 |
| Charpy Notched Impact Strength | -40°C | kJ/m² | 7.0 -- |
| 23°C | kJ/m² | 9.5 14 |
| hardness | Test Condition | Test Method | TORAY SHENZHEN/CM3004G30 BK |
|---|---|---|---|
| Rockwell hardness | R计秤,23°C | 121 -- |
| Basic performance | Test Condition | Test Method | TORAY SHENZHEN/CM3004G30 BK |
|---|---|---|---|
| Water absorption rate | 23℃，24小时 | ASTM D-570 | 1.3%水｜- % |
| Electrical performance | Test Condition | Test Method | TORAY SHENZHEN/CM3004G30 BK |
|---|---|---|---|
| dielectric strength | 1/8" | ASTM D-149 | 1.3%水｜33 KV/mm |
| Dissipation Factor | 106Hz | ASTM D-150 | 1.3%水｜- |
| dielectric constant | 23°C,1MHz | 0.0100 -- | |
| arc resistance | sec | 70.0 -- | |
| Volume resistivity | ASTM D-257 | 无水｜8×1014 Ω.cm | |
| dielectric strength | kV/mm | 38 33 | |
| arc resistance | 1/8" | ASTM D-495 | 1.3%水｜- S |
| Compared to the Leakage Traceability Index (CTI) | UL 746 | 1.3%水｜- V | |
| dielectric constant | 23°C,1kHz | 4.00 -- | |
| Volume resistivity | ohms·cm | 1E+15 1E+13 | |
| Compared to the Leakage Tracking Index (CTI) | CTI | V | PLC 3 |
| Mechanical properties | Test Condition | Test Method | TORAY SHENZHEN/CM3004G30 BK |
|---|---|---|---|
| Flexural modulus | -40°C | MPa | 10200 -- |
| 23°C | MPa | 9300 6500 | |
| bending strength | 23°C | 250 MPa | |
| Taber abraser | 1000Cycles | mg | 26.0 -- |
| tensile strength | 23°C | 165 MPa | |
| Flexural modulus | 23℃ | ASTM D-790 | 1.3%水｜65000 kg/cm2 |
| bending strength | 23℃ | ASTM D-790 | 1.3%水｜2000 kg/cm2 |
| tensile strength | -40°C | MPa | 190 -- |
| bending strength | 80°C | MPa | 150 -- |
| Tensile strain | 断裂,80°C | % | 4.5 -- |
| Impact strength of cantilever beam gap | 23℃，无缺口1/8 | 1.3%水｜70 kg.cm/cm | |
| elongation at break | 23℃ | ASTM D-638 | 1.3%水｜5 % |
| tensile strength | 23℃，断裂 | ASTM D-638 | 1.3%水｜1350 kg/cm2 |
| Tensile strain | 断裂,23°C | % | 3.0 3.0 |
| Flexural modulus | 80°C | MPa | 5500 -- |
| bending strength | -40°C | MPa | 275 -- |
| Tensile strain | 断裂,-40°C | % | 2.5 -- |
| tensile strength | 80°C | MPa | 110 -- |
| flammability | Test Condition | Test Method | TORAY SHENZHEN/CM3004G30 BK |
|---|---|---|---|
| UL flame retardant rating | 0.40mm | V-0 -- |
| physical property | Test Condition | Test Method | TORAY SHENZHEN/CM3004G30 BK |
|---|---|---|---|
| Shrinkage rate | MD:3.00mm4 | % | 0.20-0.50 -- |
| Water absorption rate | 饱和,23°C | % | 4.0 -- |
| Shrinkage rate | TD:3.00mm3 | % | 0.60-0.90 -- |
| density | ASTM D-792 | 1.3%水｜- | |
| 23°C | g/cm³ | 1.59 -- | |
| Water absorption rate | 23°C,24hr | % | 0.60 -- |
| Thermal performance | Test Condition | Test Method | TORAY SHENZHEN/CM3004G30 BK |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | °C | 251 -- |
| melting temperature | 差示扫描测热计DSC法 | 265 °C | |
| °C | 265 -- | ||
| Linear coefficient of thermal expansion | MD | cm/cm/°C | 2E-05 -- |
| ASTM D-696 | 无水｜2 10-5cm/cm.℃ | ||
| ASTM D-696 | 1.3%水｜- | ||
| UL-94 flame retardant grade | UL 94 | 1.3%水｜- | |
| Heat distortion temperature | 18.6kg/cm2，HDT | ASTM D-648 | 1.3%水｜- °C |