MPR 4060 BK USA Advanced
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | USA Advanced/ 4060 BK |
|---|---|---|---|
| Shore hardness | ShoreA,1.90mm,CompressionMolded | ISO 868 | 57 |
| DurometerHardness | ShoreA,1.90mm,CompressionMolded | ASTM D2240 | 57 |
| Mechanical properties | Test Condition | Test Method | USA Advanced/ 4060 BK |
|---|---|---|---|
| Torsion Module | 24°C,1.90mm | ASTM D1043 | 1.70 MPa |
| -20°C,1.90mm | ASTM D1043 | 6.80 MPa | |
| Taber abraser | 1000Cycles,1000g,CS-17转轮 | ASTM D1044 | 1.00 mg |
| physical property | Test Condition | Test Method | USA Advanced/ 4060 BK |
|---|---|---|---|
| density | ASTM D471 | 1.17 g/cm³ | |
| MeltViscosity | 190°C,300sec^-1 | ASTM D3835 | 370 Pa·s |
| density | ISO 2781 | 1.17 g/cm³ |
| aging | Test Condition | Test Method | USA Advanced/ 4060 BK |
|---|---|---|---|
| volume change | 27°C,168hr,inReferenceFuelB | ISO 1817 | 11 % |
| 27°C,168hr,inReferenceFuelB | ASTM D471 | 11 % | |
| 100°C,168hr,在水中 | ASTM D471 | 10 % | |
| 100°C,168hr,inIRM903Oil | ISO 1817 | 12 % | |
| Hardness change rate in the air | ShoreA,125°C,168hr | ASTM D573 | -2.0 |
| volume change | 100°C,168hr,inIRM903Oil | ASTM D471 | 12 % |
| 100°C,168hr,inASTM#1Oil | ASTM D471 | -19 % | |
| Shore hardness | ShoreA,125°C,168hr | ISO 188 | -2.0 |
| volume change | 100°C,168hr,inASTM#1Oil | ISO 1817 | -19 % |
| 100°C,168hr,在水中 | ISO 1817 | 10 % |
| elastomer | Test Condition | Test Method | USA Advanced/ 4060 BK |
|---|---|---|---|
| elongation | Break,1.90mm2 | ASTM D412 | 390 % |
| tensile strength | 100%Strain,125°C,1.90mm4 | ISO 188 | 2.70 MPa |
| Yield,125°C,1.90mm4 | ASTM D573 | 8.30 MPa | |
| Yield,125°C,1.90mm4 | ISO 188 | 8.30 MPa | |
| Yield,1.90mm2 | ASTM D412 | 7.70 MPa | |
| tear strength | 1.90mm | ASTM D624 | 33.3 kN/m |
| tensile strength | 100%Strain,1.90mm2 | ASTM D412 | 2.90 MPa |
| 100%Strain,1.90mm2 | ISO 37 | 2.90 MPa | |
| compression set | 100°C,22hr | ISO 815 | 72 % |
| tensile strength | Yield,1.90mm2 | ISO 37 | 7.70 MPa |
| 100%Strain,125°C,1.90mm4 | ASTM D573 | 2.70 MPa | |
| compression set | 100°C,22hr | ASTM D395B | 72 % |
| elongation | Break,125°C,1.90mm4 | ISO 188 | 460 % |
| Clash Mountain Module | -35°C | ASTM D1043 | 68.9 MPa |
| elongation | Break,1.90mm2 | ISO 37 | 390 % |
| compression set | 24°C,22hr | ISO 815 | 16 % |
| Stretch permanent deformation | ASTM D412 | 7 % | |
| elongation | Break,125°C,1.90mm4 | ASTM D573 | 460 % |
| compression set | 24°C,22hr | ASTM D395B | 16 % |
| Thermal performance | Test Condition | Test Method | USA Advanced/ 4060 BK |
|---|---|---|---|
| brittle temperature | ISO 812 | -74.0 °C | |
| ASTM D746 | -74.0 °C |